AB  - In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the possibility of application of such waste material. Thermal shock of the samples was conducted using water quench test. Image analysis and ultrasonic measurements were used as nondestructive methods for quantification of thermal shock damage at the surface and in the bulk of the specimens. Phase composition of samples was determined by X-ray powder diffraction (XRPD). The degradation level of samples was about 43 % after 20 cycles of water quench tests. The results pointed out that glass-ceramic material exhibited good thermal shock resistance.
PB  - Međunarodni Institut za nauku o sinterovanju, Beograd
T2  - Science of Sintering
T1  - Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit
EP  - 147
IS  - 2
SP  - 139
VL  - 49
DO  - 10.2298/SOS1702139C
ER  - 

@article{
author = "Cocić, Mira and Matović, Branko and Pošarac, Milica B. and Volkov-Husović, Tatjana and Majstorović, Jelena and Tasić, Visa and Dević, Snežana and Vusović, Nenad",
year = "2017",
abstract = "In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the possibility of application of such waste material. Thermal shock of the samples was conducted using water quench test. Image analysis and ultrasonic measurements were used as nondestructive methods for quantification of thermal shock damage at the surface and in the bulk of the specimens. Phase composition of samples was determined by X-ray powder diffraction (XRPD). The degradation level of samples was about 43 % after 20 cycles of water quench tests. The results pointed out that glass-ceramic material exhibited good thermal shock resistance.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit",
pages = "147-139",
number = "2",
volume = "49",
doi = "10.2298/SOS1702139C"
}

Cocić, M., Matović, B., Pošarac, M. B., Volkov-Husović, T., Majstorović, J., Tasić, V., Dević, S.,& Vusović, N.. (2017). Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 49(2), 139-147.
https://doi.org/10.2298/SOS1702139C

Cocić M, Matović B, Pošarac MB, Volkov-Husović T, Majstorović J, Tasić V, Dević S, Vusović N. Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit. in Science of Sintering. 2017;49(2):139-147.
doi:10.2298/SOS1702139C .

Cocić, Mira, Matović, Branko, Pošarac, Milica B., Volkov-Husović, Tatjana, Majstorović, Jelena, Tasić, Visa, Dević, Snežana, Vusović, Nenad, "Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit" in Science of Sintering, 49, no. 2 (2017):139-147,
https://doi.org/10.2298/SOS1702139C . .