abstract = "The present study focuses the cavitation resistance results of samples obtained by the Selective Laser
Sintering technology. All samples were made from Nylon 12 – Polyamide 12 powder, also known as PA2200
in the industry, produced by EOS GmbH. The powder used for building the samples represented a mixture of
50% new powder and 50% recycled powder. Samples with different section thicknesses (0.4mm; 0.8mm and
1.0mm) were subjected to the ultrasonically induced cavitation test method to investigate the effect of geometry
on their cavitation behaviour. The change in mass loss during different cavitation times was measured on the
tested samples. The morphology of cavitation damage was characterized using Scanning Electron Microscopy
(SEM). The results obtained in this paper have shown that section thickness of the samples has a significant
influence on the cavitation resistance, with the highest cavitation resistance obtained for the samples a
thickness of 0.4mm.",
publisher = "Belgrade : University, Faculty of Mechanical Engineering",
journal = "Programme and The Book of Abstracts / International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2023, 04 – 07 July 2023, Zlatibor, Serbia",
title = "EFFECT OF SECTION THICKNESS ON CAVITATION BEHAVIOUR OF SELECTIVE LASER SINTERED POLYAMIDE 12",
pages = "19",
url = "https://hdl.handle.net/21.15107/rcub_technorep_7009"
}