AB  - In this work, we investigate the role of crystallographic texture on the onset of abnormal grain growth
(AGG) in AA5182 alloy. TMP included 65% cold-rolling reduction and isothermal annealing at 480°C at
various times. The microstructure characterization by optical microscopy in polarized light revealed that
AGG starts after holding for 5 min at 480°C. Further investigation of the sample with incipient abnormal
grains was conducted by an SEM equipped with an EBSD detector. The incipient abnormal grains appear
to have an orientation of minor texture components, i.e. different cube variants, most likely due to the
enhanced grain boundary mobility. However, texture fails to explain the difference in the propensity toward
AGG in the region close to the sheet surface and its center, which is likely caused by the non-uniform
distribution of the intermetallic particles.
PB  - Bor : University of Belgrade, Technical Faculty
C3  - Proceedings / 54th International October Conference on Mining and Metallurgy - IOC 2023, 18-21 October 2023, Bor Lake, Serbia
T1  - Initiation of abnormal grain growth in cold-rolled sheet of AA5182 Al-Mg alloy: role of texture
EP  - 484
SP  - 481
UR  - https://hdl.handle.net/21.15107/rcub_technorep_7249
ER  - 

@conference{
author = "Ghulam Isaq Khan, Muhamad and Rajković, Filip and Popović, Miljana and Prelević, Dejan and Ćitić, Aleksandar and Radetić, Tamara",
year = "2023",
abstract = "In this work, we investigate the role of crystallographic texture on the onset of abnormal grain growth
(AGG) in AA5182 alloy. TMP included 65% cold-rolling reduction and isothermal annealing at 480°C at
various times. The microstructure characterization by optical microscopy in polarized light revealed that
AGG starts after holding for 5 min at 480°C. Further investigation of the sample with incipient abnormal
grains was conducted by an SEM equipped with an EBSD detector. The incipient abnormal grains appear
to have an orientation of minor texture components, i.e. different cube variants, most likely due to the
enhanced grain boundary mobility. However, texture fails to explain the difference in the propensity toward
AGG in the region close to the sheet surface and its center, which is likely caused by the non-uniform
distribution of the intermetallic particles.",
publisher = "Bor : University of Belgrade, Technical Faculty",
journal = "Proceedings / 54th International October Conference on Mining and Metallurgy - IOC 2023, 18-21 October 2023, Bor Lake, Serbia",
title = "Initiation of abnormal grain growth in cold-rolled sheet of AA5182 Al-Mg alloy: role of texture",
pages = "484-481",
url = "https://hdl.handle.net/21.15107/rcub_technorep_7249"
}

Ghulam Isaq Khan, M., Rajković, F., Popović, M., Prelević, D., Ćitić, A.,& Radetić, T.. (2023). Initiation of abnormal grain growth in cold-rolled sheet of AA5182 Al-Mg alloy: role of texture. in Proceedings / 54th International October Conference on Mining and Metallurgy - IOC 2023, 18-21 October 2023, Bor Lake, Serbia
Bor : University of Belgrade, Technical Faculty., 481-484.
https://hdl.handle.net/21.15107/rcub_technorep_7249

Ghulam Isaq Khan M, Rajković F, Popović M, Prelević D, Ćitić A, Radetić T. Initiation of abnormal grain growth in cold-rolled sheet of AA5182 Al-Mg alloy: role of texture. in Proceedings / 54th International October Conference on Mining and Metallurgy - IOC 2023, 18-21 October 2023, Bor Lake, Serbia. 2023;:481-484.
https://hdl.handle.net/21.15107/rcub_technorep_7249 .

Ghulam Isaq Khan, Muhamad, Rajković, Filip, Popović, Miljana, Prelević, Dejan, Ćitić, Aleksandar, Radetić, Tamara, "Initiation of abnormal grain growth in cold-rolled sheet of AA5182 Al-Mg alloy: role of texture" in Proceedings / 54th International October Conference on Mining and Metallurgy - IOC 2023, 18-21 October 2023, Bor Lake, Serbia (2023):481-484,
https://hdl.handle.net/21.15107/rcub_technorep_7249 .

TY  - CONF
AU  - Ghulam Isaq Khan, Muhamad
AU  - Rajković, Filip
AU  - Popović, Miljana
AU  - Prelević, Dejan
AU  - Ćitić, Aleksandar
AU  - Radetić, Tamara
PY  - 2023
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/7250
AB  - Studies of recrystallization and grain growth phenomena have a long history, but the causes of abnormal grain growth (AGG) are not well understood. We report on the results of the study of the occurrence of AGG in Al-Mg alloy AA5182. The industrially produced hot band underwent various routes of thermo-mechanical processing: inter-annealing, cold rolling with reductions ranging from 40-85% followed by isochronal anneal (1h) in the temperature range 350-520°C or isothermal treatment at 480°C for various times. The microstructural characterization was conducted by optical microscopy in polarized light and FEG SEM, while the EBSD technique was used for microtexture analysis of the selected states. The results showed that the temperature for the onset of the AGG decreases as the degree of cold reduction increases. The abnormal grains start to appear in the regions close to the surface, i.e., within 1.5 mm from it in the inter-annealed 12 mm thick hot band or 700 μm in the case of cold rolled sheet with 64% reduction. Initially equiaxed, abnormal grains show strong growth anisotropy with much faster growth in the rolling than in the normal direction. Growth anisotropy was attributed to the rod-like shape and alignment of Al6Mn dispersoids through Zener pinning. With extended annealing, bands of abnormal grains form parallel to the surfaces. Microtexture analysis of the sample with incipient abnormal grains showed the presence of retained rolling texture components in the form of R-fibre. In contrast, the incipient abnormal grains appear to have orientations of cube variants, the texture components which are at or below random level. Since the texture is similar throughout the sheet, it is likely that the AGG starts first in the surface region due to the non-uniform deformation and distribution of the intermetallic particles.
PB  - Belgrade : Institute of Technical Sciences of SASA
C3  - Program and the Book of abstracts / Twenty-first Young Researchers' Conference Materials Science and Engineering, November 29 – December 1, 2023, Belgrade, Serbia
T1  - Study of abnormal grain growth in cold-rolled AA5182 Al-Mg alloy
SP  - 61
UR  - https://hdl.handle.net/21.15107/rcub_technorep_7250
ER  - 

@conference{
author = "Ghulam Isaq Khan, Muhamad and Rajković, Filip and Popović, Miljana and Prelević, Dejan and Ćitić, Aleksandar and Radetić, Tamara",
year = "2023",
abstract = "Studies of recrystallization and grain growth phenomena have a long history, but the causes of abnormal grain growth (AGG) are not well understood. We report on the results of the study of the occurrence of AGG in Al-Mg alloy AA5182. The industrially produced hot band underwent various routes of thermo-mechanical processing: inter-annealing, cold rolling with reductions ranging from 40-85% followed by isochronal anneal (1h) in the temperature range 350-520°C or isothermal treatment at 480°C for various times. The microstructural characterization was conducted by optical microscopy in polarized light and FEG SEM, while the EBSD technique was used for microtexture analysis of the selected states. The results showed that the temperature for the onset of the AGG decreases as the degree of cold reduction increases. The abnormal grains start to appear in the regions close to the surface, i.e., within 1.5 mm from it in the inter-annealed 12 mm thick hot band or 700 μm in the case of cold rolled sheet with 64% reduction. Initially equiaxed, abnormal grains show strong growth anisotropy with much faster growth in the rolling than in the normal direction. Growth anisotropy was attributed to the rod-like shape and alignment of Al6Mn dispersoids through Zener pinning. With extended annealing, bands of abnormal grains form parallel to the surfaces. Microtexture analysis of the sample with incipient abnormal grains showed the presence of retained rolling texture components in the form of R-fibre. In contrast, the incipient abnormal grains appear to have orientations of cube variants, the texture components which are at or below random level. Since the texture is similar throughout the sheet, it is likely that the AGG starts first in the surface region due to the non-uniform deformation and distribution of the intermetallic particles.",
publisher = "Belgrade : Institute of Technical Sciences of SASA",
journal = "Program and the Book of abstracts / Twenty-first Young Researchers' Conference Materials Science and Engineering, November 29 – December 1, 2023, Belgrade, Serbia",
title = "Study of abnormal grain growth in cold-rolled AA5182 Al-Mg alloy",
pages = "61",
url = "https://hdl.handle.net/21.15107/rcub_technorep_7250"
}

Ghulam Isaq Khan, M., Rajković, F., Popović, M., Prelević, D., Ćitić, A.,& Radetić, T.. (2023). Study of abnormal grain growth in cold-rolled AA5182 Al-Mg alloy. in Program and the Book of abstracts / Twenty-first Young Researchers' Conference Materials Science and Engineering, November 29 – December 1, 2023, Belgrade, Serbia
Belgrade : Institute of Technical Sciences of SASA., 61.
https://hdl.handle.net/21.15107/rcub_technorep_7250

Ghulam Isaq Khan M, Rajković F, Popović M, Prelević D, Ćitić A, Radetić T. Study of abnormal grain growth in cold-rolled AA5182 Al-Mg alloy. in Program and the Book of abstracts / Twenty-first Young Researchers' Conference Materials Science and Engineering, November 29 – December 1, 2023, Belgrade, Serbia. 2023;:61.
https://hdl.handle.net/21.15107/rcub_technorep_7250 .

Ghulam Isaq Khan, Muhamad, Rajković, Filip, Popović, Miljana, Prelević, Dejan, Ćitić, Aleksandar, Radetić, Tamara, "Study of abnormal grain growth in cold-rolled AA5182 Al-Mg alloy" in Program and the Book of abstracts / Twenty-first Young Researchers' Conference Materials Science and Engineering, November 29 – December 1, 2023, Belgrade, Serbia (2023):61,
https://hdl.handle.net/21.15107/rcub_technorep_7250 .