AB  - Zinc alloy coatings electrochemically deposited on steel from electrolytes with different components differ in their composition, homogeneity, porosity, structure and other characteristics that affect their corrosion resistance. Manganese is characterized by a very negative electrochemical potential and very high strength, prompting many researchers to study Zn-Mn alloys for the anti-corrosion purposes in the industry, especially automotive. In this work it was examined the influence of the type of the electrolyte deposition on the current efficiency during electrodeposition of Zn-Mn alloys. Zn-Mn alloys were deposited on steel from chloride, sulphate and pyrophosphate plating baths at different current densities. We have examined the influence of deposition current density on the current efficiency during electrodeposition, appearance of alloy coatings, as well as their corrosion stability. It was shown that Zn-Mn alloys with the best corrosion properties, among all examined ones, were obtained from chloride plating bath at 2 A dm-2.
AB  - Превлаке легура цинка електрохемијски добијене из електролита са различитим компонентама имају разлике у свом саставу, хомогености, порозности, структури и другим карактеристикама које утичу на њихову корозиону отпорност. Манган се одликује јако негативним електрохемијским потенцијалом и јако великом чврстоћом, што је навело многе истраживаче на испитивања легуре Zn-Mn у антикорозионе сврхе, за потребе у индустрији, нарочито аутомобилској. У овом раду испитиван је утицај врсте електролита на таложење Zn-Mn легура, као и на искоришћење струје приликом електрохемијског таложења. Легуре су таложене на челику из хлоридног, сулфатног и пирофосфатног електролита различитим густинама струје. При задатим условима таложења испитиван је хемијски састав, храпавост, изглед превлака легура, и њиховa корозиона стабилност. Показано је да највећу корозиону стабилност имају легуре добијене таложењем из хлоридног електролита густином струје од
2 A dm-2.
PB  - Academy of Sciences and Arts of Republic of Srpska
T2  - Contemporary Materials
T1  - Corrosion stability of electrochemically deposited Zn-Mn alloy coatings
T1  - Корозиона стабилност превлака Zn-Mn легура добијених електрохемијским путем
EP  - 93
IS  - 1
SP  - 87
VL  - 1
DO  - 10.5767/anurs.cmat.100101.en.087T
ER  - 

@article{
author = "Tomić, M. V. and Bučko, M. M. and Pavlović, M. G. and Bajat, J. B.",
year = "2010",
abstract = "Zinc alloy coatings electrochemically deposited on steel from electrolytes with different components differ in their composition, homogeneity, porosity, structure and other characteristics that affect their corrosion resistance. Manganese is characterized by a very negative electrochemical potential and very high strength, prompting many researchers to study Zn-Mn alloys for the anti-corrosion purposes in the industry, especially automotive. In this work it was examined the influence of the type of the electrolyte deposition on the current efficiency during electrodeposition of Zn-Mn alloys. Zn-Mn alloys were deposited on steel from chloride, sulphate and pyrophosphate plating baths at different current densities. We have examined the influence of deposition current density on the current efficiency during electrodeposition, appearance of alloy coatings, as well as their corrosion stability. It was shown that Zn-Mn alloys with the best corrosion properties, among all examined ones, were obtained from chloride plating bath at 2 A dm-2., Превлаке легура цинка електрохемијски добијене из електролита са различитим компонентама имају разлике у свом саставу, хомогености, порозности, структури и другим карактеристикама које утичу на њихову корозиону отпорност. Манган се одликује јако негативним електрохемијским потенцијалом и јако великом чврстоћом, што је навело многе истраживаче на испитивања легуре Zn-Mn у антикорозионе сврхе, за потребе у индустрији, нарочито аутомобилској. У овом раду испитиван је утицај врсте електролита на таложење Zn-Mn легура, као и на искоришћење струје приликом електрохемијског таложења. Легуре су таложене на челику из хлоридног, сулфатног и пирофосфатног електролита различитим густинама струје. При задатим условима таложења испитиван је хемијски састав, храпавост, изглед превлака легура, и њиховa корозиона стабилност. Показано је да највећу корозиону стабилност имају легуре добијене таложењем из хлоридног електролита густином струје од
2 A dm-2.",
publisher = "Academy of Sciences and Arts of Republic of Srpska",
journal = "Contemporary Materials",
title = "Corrosion stability of electrochemically deposited Zn-Mn alloy coatings, Корозиона стабилност превлака Zn-Mn легура добијених електрохемијским путем",
pages = "93-87",
number = "1",
volume = "1",
doi = "10.5767/anurs.cmat.100101.en.087T"
}

Tomić, M. V., Bučko, M. M., Pavlović, M. G.,& Bajat, J. B.. (2010). Corrosion stability of electrochemically deposited Zn-Mn alloy coatings. in Contemporary Materials
Academy of Sciences and Arts of Republic of Srpska., 1(1), 87-93.
https://doi.org/10.5767/anurs.cmat.100101.en.087T

Tomić MV, Bučko MM, Pavlović MG, Bajat JB. Corrosion stability of electrochemically deposited Zn-Mn alloy coatings. in Contemporary Materials. 2010;1(1):87-93.
doi:10.5767/anurs.cmat.100101.en.087T .

Tomić, M. V., Bučko, M. M., Pavlović, M. G., Bajat, J. B., "Corrosion stability of electrochemically deposited Zn-Mn alloy coatings" in Contemporary Materials, 1, no. 1 (2010):87-93,
https://doi.org/10.5767/anurs.cmat.100101.en.087T . .