AB  - In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the possibility of application of such waste material. Thermal shock of the samples was conducted using water quench test. Image analysis and ultrasonic measurements were used as nondestructive methods for quantification of thermal shock damage at the surface and in the bulk of the specimens. Phase composition of samples was determined by X-ray powder diffraction (XRPD). The degradation level of samples was about 43 % after 20 cycles of water quench tests. The results pointed out that glass-ceramic material exhibited good thermal shock resistance.
PB  - Međunarodni Institut za nauku o sinterovanju, Beograd
T2  - Science of Sintering
T1  - Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit
EP  - 147
IS  - 2
SP  - 139
VL  - 49
DO  - 10.2298/SOS1702139C
ER  - 

@article{
author = "Cocić, Mira and Matović, Branko and Pošarac, Milica B. and Volkov-Husović, Tatjana and Majstorović, Jelena and Tasić, Visa and Dević, Snežana and Vusović, Nenad",
year = "2017",
abstract = "In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the possibility of application of such waste material. Thermal shock of the samples was conducted using water quench test. Image analysis and ultrasonic measurements were used as nondestructive methods for quantification of thermal shock damage at the surface and in the bulk of the specimens. Phase composition of samples was determined by X-ray powder diffraction (XRPD). The degradation level of samples was about 43 % after 20 cycles of water quench tests. The results pointed out that glass-ceramic material exhibited good thermal shock resistance.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit",
pages = "147-139",
number = "2",
volume = "49",
doi = "10.2298/SOS1702139C"
}

Cocić, M., Matović, B., Pošarac, M. B., Volkov-Husović, T., Majstorović, J., Tasić, V., Dević, S.,& Vusović, N.. (2017). Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 49(2), 139-147.
https://doi.org/10.2298/SOS1702139C

Cocić M, Matović B, Pošarac MB, Volkov-Husović T, Majstorović J, Tasić V, Dević S, Vusović N. Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit. in Science of Sintering. 2017;49(2):139-147.
doi:10.2298/SOS1702139C .

Cocić, Mira, Matović, Branko, Pošarac, Milica B., Volkov-Husović, Tatjana, Majstorović, Jelena, Tasić, Visa, Dević, Snežana, Vusović, Nenad, "Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit" in Science of Sintering, 49, no. 2 (2017):139-147,
https://doi.org/10.2298/SOS1702139C . .

TY  - JOUR
AU  - Cocić, Mira
AU  - Logar, Mihovil
AU  - Matović, Branko
AU  - Dević, Snežana
AU  - Volkov-Husović, Tatjana
AU  - Cocić, Sasa
AU  - Tasić, Visa
PY  - 2016
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3341
AB  - In the copper extraction, especially during the process of flotation enrichment and the pyrometallurgical processing, the waste materials that represent huge polluters of environment are being generated. In order to examine the application of Final flotation waste (FFW) in the manufacturing of new materials from the glass-ceramic group phase and mineral composition were examined as well as thermal properties. FFW kinetics of sintering has been tested at different dyamics (1 degrees C/min, 29 degrees C/min and 43 degrees C/min), in order to find the optimum conditions for sintering with a minimum amount of energy and time consumption. The samples were examined using: X-ray diffraction, X-ray fluorescence analysis, SEM (Scanning Electron Microscopy) and thermal microscopy. The best results for the production of glass ceramic materials were obtained during the sintering at heating regime of 29 degrees C/min.
PB  - Međunarodni Institut za nauku o sinterovanju, Beograd
T2  - Science of Sintering
T1  - Final Flotation Waste Kinetics of Sintering at Different Heating Regimes
EP  - 208
IS  - 2
SP  - 197
VL  - 48
DO  - 10.2298/SOS1602197C
ER  - 

@article{
author = "Cocić, Mira and Logar, Mihovil and Matović, Branko and Dević, Snežana and Volkov-Husović, Tatjana and Cocić, Sasa and Tasić, Visa",
year = "2016",
abstract = "In the copper extraction, especially during the process of flotation enrichment and the pyrometallurgical processing, the waste materials that represent huge polluters of environment are being generated. In order to examine the application of Final flotation waste (FFW) in the manufacturing of new materials from the glass-ceramic group phase and mineral composition were examined as well as thermal properties. FFW kinetics of sintering has been tested at different dyamics (1 degrees C/min, 29 degrees C/min and 43 degrees C/min), in order to find the optimum conditions for sintering with a minimum amount of energy and time consumption. The samples were examined using: X-ray diffraction, X-ray fluorescence analysis, SEM (Scanning Electron Microscopy) and thermal microscopy. The best results for the production of glass ceramic materials were obtained during the sintering at heating regime of 29 degrees C/min.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Final Flotation Waste Kinetics of Sintering at Different Heating Regimes",
pages = "208-197",
number = "2",
volume = "48",
doi = "10.2298/SOS1602197C"
}

Cocić, M., Logar, M., Matović, B., Dević, S., Volkov-Husović, T., Cocić, S.,& Tasić, V.. (2016). Final Flotation Waste Kinetics of Sintering at Different Heating Regimes. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 48(2), 197-208.
https://doi.org/10.2298/SOS1602197C

Cocić M, Logar M, Matović B, Dević S, Volkov-Husović T, Cocić S, Tasić V. Final Flotation Waste Kinetics of Sintering at Different Heating Regimes. in Science of Sintering. 2016;48(2):197-208.
doi:10.2298/SOS1602197C .

Cocić, Mira, Logar, Mihovil, Matović, Branko, Dević, Snežana, Volkov-Husović, Tatjana, Cocić, Sasa, Tasić, Visa, "Final Flotation Waste Kinetics of Sintering at Different Heating Regimes" in Science of Sintering, 48, no. 2 (2016):197-208,
https://doi.org/10.2298/SOS1602197C . .

TY  - JOUR
AU  - Živković, Dragana
AU  - Manasijević, Dragan
AU  - Kamberović, Željko
AU  - Cocić, Mira
AU  - Marjanović, B.
PY  - 2007
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/1034
AB  - The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution mode!, are presented in the paper. Obtained data for partial and integral molar thermodynamic quantities in the temperature interval 1000-1200K are given. The characterization of these alloys have been done using DTA, XRD, SEM and optic microscopy, which enabled the construction of the Ag-In-Sb phase diagram in the concentration range up to 60 wt. % Ag.
PB  - Croatian Metallurgical Society
T2  - Metalurgija
T1  - Thermodynamic and structural investigation of the Ag-In-Sb system
EP  - 156
IS  - 3
SP  - 151
VL  - 46
UR  - https://hdl.handle.net/21.15107/rcub_technorep_1034
ER  - 

@article{
author = "Živković, Dragana and Manasijević, Dragan and Kamberović, Željko and Cocić, Mira and Marjanović, B.",
year = "2007",
abstract = "The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution mode!, are presented in the paper. Obtained data for partial and integral molar thermodynamic quantities in the temperature interval 1000-1200K are given. The characterization of these alloys have been done using DTA, XRD, SEM and optic microscopy, which enabled the construction of the Ag-In-Sb phase diagram in the concentration range up to 60 wt. % Ag.",
publisher = "Croatian Metallurgical Society",
journal = "Metalurgija",
title = "Thermodynamic and structural investigation of the Ag-In-Sb system",
pages = "156-151",
number = "3",
volume = "46",
url = "https://hdl.handle.net/21.15107/rcub_technorep_1034"
}

Živković, D., Manasijević, D., Kamberović, Ž., Cocić, M.,& Marjanović, B.. (2007). Thermodynamic and structural investigation of the Ag-In-Sb system. in Metalurgija
Croatian Metallurgical Society., 46(3), 151-156.
https://hdl.handle.net/21.15107/rcub_technorep_1034

Živković D, Manasijević D, Kamberović Ž, Cocić M, Marjanović B. Thermodynamic and structural investigation of the Ag-In-Sb system. in Metalurgija. 2007;46(3):151-156.
https://hdl.handle.net/21.15107/rcub_technorep_1034 .

Živković, Dragana, Manasijević, Dragan, Kamberović, Željko, Cocić, Mira, Marjanović, B., "Thermodynamic and structural investigation of the Ag-In-Sb system" in Metalurgija, 46, no. 3 (2007):151-156,
https://hdl.handle.net/21.15107/rcub_technorep_1034 .