TY  - JOUR
AU  - Radovanović, Lidija
AU  - Radovanović, Željko
AU  - Simović, Bojana
AU  - Vasić, Milica V.
AU  - Balanč, Bojana
AU  - Dapčević, Aleksandra
AU  - Dramićanin, Miroslav D.
AU  - Rogan, Jelena
PY  - 2023
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5984
AB  - A biphasic [Mn(dipya)(H2O)4](tpht)/{[Zn(dipya)(tpht)]·H2O}n com­plex material, I (dipya = 2,2’-dipyridylamine, tpht2– = dianion of terephthalatic acid) was synthesized by ligand exchange reaction and characterized by XRPD and FTIR spectroscopy. A ZnO/ZnMn2O4 composite, II, has been prepared via thermal decomposition of I in an air atmosphere at 450 °C. XRPD, FTIR and FESEM analyses of II revealed the simultaneous presence of spherical nano­particles of wurtzite ZnO and elongated nanoparticles of spinel ZnMn2O4. The specific surface area of II was determined by the BET method, whereas the volume and average size of the mesopores were calculated in accordance with the BJH method. The measurements of the mean size, polydispersity index and zeta potential showed colloidal instability of II. Two band gap values of 2.4 and 3.3 eV were determined using UV–Vis diffuse reflectance spectroscopy, while the measurements of photoluminescence revealed that II is active in the blue region of the visible spectrum. Testing of composite II as a pigmentary material showed that it can be used for the colouring of a ceramic glaze.
AB  - Двофазни  [Mn(dipya)(H2O)4](tpht)/{[Zn(dipya)(tpht)]·H2O}n комплексни материјал, I,  (dipya  =  2,2’-дипиридиламин,  tpht2–  =  дианјон  1,4-бензендикарбоксилнекиселине) синтетисан је реакцијом измене лиганада и окарактерисан XRPD мeтoдоми FTIR спек-троскопијом. Композит ZnO/ZnMn2O4, II, добијен је термичком разградњом прекурcopa I у атмосфери ваздуха на  450  °C.  XRPD  мeтoдом,  FTIR  спектроскопијом и  FESEM  микроскопијом композита II утврђено је истовремено присуство сферних наночестица ZnO вирцитне структуре и издужених наночестица  ZnMn2O4 са структуром спинела. Специфична површина композита II одређена је BET методом, док су запремина и просечна величина мезопора израчунати у складу са  BJH  методом. Средња величина, индекс полидисперзије и цета потенцијал измерени су фотонском корелационом спектроскопијом и електрофоретским расејањем светлости и показали су нестабилност композита II. Вредности ширине забрањене зоне од  2,4  и  3,3  eV  одређене су  UV–Vis  дифузно-рефлексионом спектроскопијом, док су мерења фотолуминесценције показала да је композит II активан у плавој области видљивог дела спектра. Испитивање композита II као пигментног материјала показало је да се може користити за бојење керамичке глазуре.
PB  - Serbian Chemical Society
T2  - Journal of the Serbian Chemical Society
T1  - Structure and properties of ZnO/ZnMn2O4 composite obtained by thermal decomposition of terephthalate precursor
T1  - Структура и својства композита ZnO/ZnMn2O4 добијеног термичком разградњом терефталат-прекурсора
EP  - 325
IS  - 3
SP  - 313
VL  - 88
DO  - 10.2298/JSC221102090R
ER  - 

@article{
author = "Radovanović, Lidija and Radovanović, Željko and Simović, Bojana and Vasić, Milica V. and Balanč, Bojana and Dapčević, Aleksandra and Dramićanin, Miroslav D. and Rogan, Jelena",
year = "2023",
abstract = "A biphasic [Mn(dipya)(H2O)4](tpht)/{[Zn(dipya)(tpht)]·H2O}n com­plex material, I (dipya = 2,2’-dipyridylamine, tpht2– = dianion of terephthalatic acid) was synthesized by ligand exchange reaction and characterized by XRPD and FTIR spectroscopy. A ZnO/ZnMn2O4 composite, II, has been prepared via thermal decomposition of I in an air atmosphere at 450 °C. XRPD, FTIR and FESEM analyses of II revealed the simultaneous presence of spherical nano­particles of wurtzite ZnO and elongated nanoparticles of spinel ZnMn2O4. The specific surface area of II was determined by the BET method, whereas the volume and average size of the mesopores were calculated in accordance with the BJH method. The measurements of the mean size, polydispersity index and zeta potential showed colloidal instability of II. Two band gap values of 2.4 and 3.3 eV were determined using UV–Vis diffuse reflectance spectroscopy, while the measurements of photoluminescence revealed that II is active in the blue region of the visible spectrum. Testing of composite II as a pigmentary material showed that it can be used for the colouring of a ceramic glaze., Двофазни  [Mn(dipya)(H2O)4](tpht)/{[Zn(dipya)(tpht)]·H2O}n комплексни материјал, I,  (dipya  =  2,2’-дипиридиламин,  tpht2–  =  дианјон  1,4-бензендикарбоксилнекиселине) синтетисан је реакцијом измене лиганада и окарактерисан XRPD мeтoдоми FTIR спек-троскопијом. Композит ZnO/ZnMn2O4, II, добијен је термичком разградњом прекурcopa I у атмосфери ваздуха на  450  °C.  XRPD  мeтoдом,  FTIR  спектроскопијом и  FESEM  микроскопијом композита II утврђено је истовремено присуство сферних наночестица ZnO вирцитне структуре и издужених наночестица  ZnMn2O4 са структуром спинела. Специфична површина композита II одређена је BET методом, док су запремина и просечна величина мезопора израчунати у складу са  BJH  методом. Средња величина, индекс полидисперзије и цета потенцијал измерени су фотонском корелационом спектроскопијом и електрофоретским расејањем светлости и показали су нестабилност композита II. Вредности ширине забрањене зоне од  2,4  и  3,3  eV  одређене су  UV–Vis  дифузно-рефлексионом спектроскопијом, док су мерења фотолуминесценције показала да је композит II активан у плавој области видљивог дела спектра. Испитивање композита II као пигментног материјала показало је да се може користити за бојење керамичке глазуре.",
publisher = "Serbian Chemical Society",
journal = "Journal of the Serbian Chemical Society",
title = "Structure and properties of ZnO/ZnMn2O4 composite obtained by thermal decomposition of terephthalate precursor, Структура и својства композита ZnO/ZnMn2O4 добијеног термичком разградњом терефталат-прекурсора",
pages = "325-313",
number = "3",
volume = "88",
doi = "10.2298/JSC221102090R"
}

Radovanović, L., Radovanović, Ž., Simović, B., Vasić, M. V., Balanč, B., Dapčević, A., Dramićanin, M. D.,& Rogan, J.. (2023). Structure and properties of ZnO/ZnMn2O4 composite obtained by thermal decomposition of terephthalate precursor. in Journal of the Serbian Chemical Society
Serbian Chemical Society., 88(3), 313-325.
https://doi.org/10.2298/JSC221102090R

Radovanović L, Radovanović Ž, Simović B, Vasić MV, Balanč B, Dapčević A, Dramićanin MD, Rogan J. Structure and properties of ZnO/ZnMn2O4 composite obtained by thermal decomposition of terephthalate precursor. in Journal of the Serbian Chemical Society. 2023;88(3):313-325.
doi:10.2298/JSC221102090R .

Radovanović, Lidija, Radovanović, Željko, Simović, Bojana, Vasić, Milica V., Balanč, Bojana, Dapčević, Aleksandra, Dramićanin, Miroslav D., Rogan, Jelena, "Structure and properties of ZnO/ZnMn2O4 composite obtained by thermal decomposition of terephthalate precursor" in Journal of the Serbian Chemical Society, 88, no. 3 (2023):313-325,
https://doi.org/10.2298/JSC221102090R . .