TY  - CONF
AU  - Milošević, Marija D.
AU  - Ivanovska, Aleksandra M.
AU  - Kostić, Mirjana M.
AU  - Svirčev, Zorica B.
PY  - 2023
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/6557
AB  - Sodium alginate aqueous solutions of different concentrations (0.5, 1.0, or 2.0%) were
used for improving the sorption properties (evaluated through the determination of water
retention power (WRP) and wetting time (WT)) of raw jute fabric. The influence of drying
conditions (never-dried samples, samples dried at 60 °C or at room temperature) on the
sorption properties of alginate-treated jute fabrics was also studied. Independently on the
examined method (centrifuge or water absorption method), the same trend of improvement
in WRP of alginate-treated fabrics was observed. The WRP of never-dried fabric treated
with 2.0% sodium alginate solution determined using the water absorption or centrifuge
method increased by 4.8 or 3.3 times compared to raw jute fabric, respectively. Moreover,
the WT of jute fabrics decreased from 206.9±6.6 s down to 1.7±0.1 s after the treatment
with 0.5% sodium alginate solution. The improved sorption properties of alginate-treated
jute fabrics are attributed to the alginate layer on the fabric surface having a higher number
of accessible carboxyl groups as well as hydroxyl groups capable of forming new
hydrogen bonds with water molecules.
AB  - Vodeni rastvori natrijum-alginata različitih koncentracija (0,5, 1,0 ili 2,0%) korišćeni su za
poboljšanje sorpcionih svojstava (procenjenih određivanjem sposobnosti zadržavanja vode
(WRP) i vremena kvašenja (WT)) sirove tkanine jute. Takođe je proučavan uticaj uslova
sušenja (neosušeni uzorci, uzorci sušeni na 60 °C ili na sobnoj temperaturi) na sorpciona
svojstva tkanina jute tretiranih alginatom. Nezavisno od metode ispitivanja
(centrifugiranjem ili apsorpcijom vode posle potapanja), dobijen je isti trend poboljšanja
sposobnosti zadržavanja vode tkanina tretiranih alginatom. Sposobnost zadržavanja vode
nesušene tkanine tretirane 2,0% rastvorom natrijum-alginata, određene metodom
apsorpcije vode posle potapanja ili centrifugiranjem, povećana je 4,8 ili 3,3 puta u poređenju sa sirovom tkaninom jute, respektivno. Štaviše, tretman tkanina jute 0,5%
rastvorom natrijum-alginata dovodi do smanjenja vremena kvašenja sa 206,9±6,6 s na
1,7±0,1 s. Poboljšana sorpciona svojstva tkanina jute tretiranih alginatom pripisuju se sloju
alginata na njihovoj površini sa većim brojem dostupnih karboksilnihi hidroksilnih grupa
sposobnih da formiraju nove vodonične veze sa molekulima vode.
PB  - Beograd : Srpsko hemijsko društvo
C3  - Kratki izvodi radova ; Knjiga radova / 59. savetovanje Srpskog hemijskog društva, Novi Sad 1. i 2. jun 2023. godine
T1  - A way to improve the sorption properties of raw jute fabric by sodium alginate treatment
T1  - Tretman natrijum-alginatom kao način da se poboljšaju sorpciona svojstva sirove tkanine jute
EP  - 179
SP  - 176
UR  - https://hdl.handle.net/21.15107/rcub_technorep_6557
ER  - 

@conference{
author = "Milošević, Marija D. and Ivanovska, Aleksandra M. and Kostić, Mirjana M. and Svirčev, Zorica B.",
year = "2023",
abstract = "Sodium alginate aqueous solutions of different concentrations (0.5, 1.0, or 2.0%) were
used for improving the sorption properties (evaluated through the determination of water
retention power (WRP) and wetting time (WT)) of raw jute fabric. The influence of drying
conditions (never-dried samples, samples dried at 60 °C or at room temperature) on the
sorption properties of alginate-treated jute fabrics was also studied. Independently on the
examined method (centrifuge or water absorption method), the same trend of improvement
in WRP of alginate-treated fabrics was observed. The WRP of never-dried fabric treated
with 2.0% sodium alginate solution determined using the water absorption or centrifuge
method increased by 4.8 or 3.3 times compared to raw jute fabric, respectively. Moreover,
the WT of jute fabrics decreased from 206.9±6.6 s down to 1.7±0.1 s after the treatment
with 0.5% sodium alginate solution. The improved sorption properties of alginate-treated
jute fabrics are attributed to the alginate layer on the fabric surface having a higher number
of accessible carboxyl groups as well as hydroxyl groups capable of forming new
hydrogen bonds with water molecules., Vodeni rastvori natrijum-alginata različitih koncentracija (0,5, 1,0 ili 2,0%) korišćeni su za
poboljšanje sorpcionih svojstava (procenjenih određivanjem sposobnosti zadržavanja vode
(WRP) i vremena kvašenja (WT)) sirove tkanine jute. Takođe je proučavan uticaj uslova
sušenja (neosušeni uzorci, uzorci sušeni na 60 °C ili na sobnoj temperaturi) na sorpciona
svojstva tkanina jute tretiranih alginatom. Nezavisno od metode ispitivanja
(centrifugiranjem ili apsorpcijom vode posle potapanja), dobijen je isti trend poboljšanja
sposobnosti zadržavanja vode tkanina tretiranih alginatom. Sposobnost zadržavanja vode
nesušene tkanine tretirane 2,0% rastvorom natrijum-alginata, određene metodom
apsorpcije vode posle potapanja ili centrifugiranjem, povećana je 4,8 ili 3,3 puta u poređenju sa sirovom tkaninom jute, respektivno. Štaviše, tretman tkanina jute 0,5%
rastvorom natrijum-alginata dovodi do smanjenja vremena kvašenja sa 206,9±6,6 s na
1,7±0,1 s. Poboljšana sorpciona svojstva tkanina jute tretiranih alginatom pripisuju se sloju
alginata na njihovoj površini sa većim brojem dostupnih karboksilnihi hidroksilnih grupa
sposobnih da formiraju nove vodonične veze sa molekulima vode.",
publisher = "Beograd : Srpsko hemijsko društvo",
journal = "Kratki izvodi radova ; Knjiga radova / 59. savetovanje Srpskog hemijskog društva, Novi Sad 1. i 2. jun 2023. godine",
title = "A way to improve the sorption properties of raw jute fabric by sodium alginate treatment, Tretman natrijum-alginatom kao način da se poboljšaju sorpciona svojstva sirove tkanine jute",
pages = "179-176",
url = "https://hdl.handle.net/21.15107/rcub_technorep_6557"
}

Milošević, M. D., Ivanovska, A. M., Kostić, M. M.,& Svirčev, Z. B.. (2023). A way to improve the sorption properties of raw jute fabric by sodium alginate treatment. in Kratki izvodi radova ; Knjiga radova / 59. savetovanje Srpskog hemijskog društva, Novi Sad 1. i 2. jun 2023. godine
Beograd : Srpsko hemijsko društvo., 176-179.
https://hdl.handle.net/21.15107/rcub_technorep_6557

Milošević MD, Ivanovska AM, Kostić MM, Svirčev ZB. A way to improve the sorption properties of raw jute fabric by sodium alginate treatment. in Kratki izvodi radova ; Knjiga radova / 59. savetovanje Srpskog hemijskog društva, Novi Sad 1. i 2. jun 2023. godine. 2023;:176-179.
https://hdl.handle.net/21.15107/rcub_technorep_6557 .

Milošević, Marija D., Ivanovska, Aleksandra M., Kostić, Mirjana M., Svirčev, Zorica B., "A way to improve the sorption properties of raw jute fabric by sodium alginate treatment" in Kratki izvodi radova ; Knjiga radova / 59. savetovanje Srpskog hemijskog društva, Novi Sad 1. i 2. jun 2023. godine (2023):176-179,
https://hdl.handle.net/21.15107/rcub_technorep_6557 .

TY  - CONF
AU  - Ivanovska, Aleksandra M.
AU  - Branković, Ivana D.
AU  - Milošević, Marija D.
AU  - Kostić, Mirjana M.
AU  - Svirčev, Zorica B.
PY  - 2022
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/6574
AB  - This work aims to obtain jute fabrics with improved sorption properties that could be used
as a novel solution for biodegraded land rehabilitation. For that purpose, raw jute fabric
was oxidized with 0.4% sodium periodate (NaIO4), while the adsorption of textile dye
Congo Red (CR) was used as an indicator for fabrics' sorption properties. The kinetic study
revealed that fabric oxidized for 60 min reached equilibrium dye adsorption after 270 min,
while in the case of jute oxidized for 120 min, the equilibrium was attained 30 min faster.
This behavior is ascribed to the better availability and higher content of functional groups
(capable of binding CR) within fabric oxidized for 120 min than within those oxidized for
60 min. The above-mentioned could be also used as an explanation for the 35 and 50%
higher adsorption capacities of fabrics oxidized for 60 and 120 min compared to the raw
fabric, respectively. With increasing the initial concentration of CR from 25 up to 100 mg
L-1, the equilibrium adsorption increased up to 2.6 times.
AB  - Cilj ovog rada je dobijanje tkanine od jute sa poboljšanim sorpcionim svojstvima koja ce
se koristititi za rehabilitaciju degradiranog zemljišta. U tu svrhu, sirova tkanina jute
oksidisana je 0,4% rastvora natrijum-perjodata (NaIO4), dok je adsorpcija tekstilne boje
Kongo crvenog (CR) korišcena kao indikator sorpcionih svojstava. Kineticka istraživanja
pokazala su da je tkanina oksidisana tokom 60 minuta dostigla ravnotežnu adsorpciju boje
nakon 270 minuta, dok je u slucaju tkanine od jute oksidisane tokom 120 minuta ravnoteža
postignuta 30 minuta brže. Ovakvo ponašanje posledica je bolje dostupnosti i veceg
sadržaja funkcionalnih grupa (sposobnih da vežu CR) unutar tkanine oksidisane tokom 120
minuta u odnosu na tkaninu oksidisanu tokom 60 minuta. Navedeno bi se moglo koristiti i
kao objašnjenje za 35 i 50% vece adsorpcione kapacitete uzoraka tkanine oksidisanih
tokom 60 i 120 minuta u pore enju sa sirovom tkaninom, redosledno . Sa povecanjem
pocetne koncentracije CR sa 25 na 100 mg L-1, ravnotežna adsorpcija se povecava do 2,6
puta.
PB  - Beograd : Srpsko hemijsko društvo
C3  - Kratki izvodi radova ; Knjiga radova / 58. savetovanje Srpskog hemijskog društva, Beograd, 9. i 10. jun 2022. godine
T1  - Adsorption of Congo Red as an indicator for the oxidized jute fabric's sorption properties
T1  - Adsorpcija Kongo crvenog kao indikatora sorpcionih svojstava oksidisane tkanine od jute
EP  - 215
SP  - 212
UR  - https://hdl.handle.net/21.15107/rcub_technorep_6574
ER  - 

@conference{
author = "Ivanovska, Aleksandra M. and Branković, Ivana D. and Milošević, Marija D. and Kostić, Mirjana M. and Svirčev, Zorica B.",
year = "2022",
abstract = "This work aims to obtain jute fabrics with improved sorption properties that could be used
as a novel solution for biodegraded land rehabilitation. For that purpose, raw jute fabric
was oxidized with 0.4% sodium periodate (NaIO4), while the adsorption of textile dye
Congo Red (CR) was used as an indicator for fabrics' sorption properties. The kinetic study
revealed that fabric oxidized for 60 min reached equilibrium dye adsorption after 270 min,
while in the case of jute oxidized for 120 min, the equilibrium was attained 30 min faster.
This behavior is ascribed to the better availability and higher content of functional groups
(capable of binding CR) within fabric oxidized for 120 min than within those oxidized for
60 min. The above-mentioned could be also used as an explanation for the 35 and 50%
higher adsorption capacities of fabrics oxidized for 60 and 120 min compared to the raw
fabric, respectively. With increasing the initial concentration of CR from 25 up to 100 mg
L-1, the equilibrium adsorption increased up to 2.6 times., Cilj ovog rada je dobijanje tkanine od jute sa poboljšanim sorpcionim svojstvima koja ce
se koristititi za rehabilitaciju degradiranog zemljišta. U tu svrhu, sirova tkanina jute
oksidisana je 0,4% rastvora natrijum-perjodata (NaIO4), dok je adsorpcija tekstilne boje
Kongo crvenog (CR) korišcena kao indikator sorpcionih svojstava. Kineticka istraživanja
pokazala su da je tkanina oksidisana tokom 60 minuta dostigla ravnotežnu adsorpciju boje
nakon 270 minuta, dok je u slucaju tkanine od jute oksidisane tokom 120 minuta ravnoteža
postignuta 30 minuta brže. Ovakvo ponašanje posledica je bolje dostupnosti i veceg
sadržaja funkcionalnih grupa (sposobnih da vežu CR) unutar tkanine oksidisane tokom 120
minuta u odnosu na tkaninu oksidisanu tokom 60 minuta. Navedeno bi se moglo koristiti i
kao objašnjenje za 35 i 50% vece adsorpcione kapacitete uzoraka tkanine oksidisanih
tokom 60 i 120 minuta u pore enju sa sirovom tkaninom, redosledno . Sa povecanjem
pocetne koncentracije CR sa 25 na 100 mg L-1, ravnotežna adsorpcija se povecava do 2,6
puta.",
publisher = "Beograd : Srpsko hemijsko društvo",
journal = "Kratki izvodi radova ; Knjiga radova / 58. savetovanje Srpskog hemijskog društva, Beograd, 9. i 10. jun 2022. godine",
title = "Adsorption of Congo Red as an indicator for the oxidized jute fabric's sorption properties, Adsorpcija Kongo crvenog kao indikatora sorpcionih svojstava oksidisane tkanine od jute",
pages = "215-212",
url = "https://hdl.handle.net/21.15107/rcub_technorep_6574"
}

Ivanovska, A. M., Branković, I. D., Milošević, M. D., Kostić, M. M.,& Svirčev, Z. B.. (2022). Adsorption of Congo Red as an indicator for the oxidized jute fabric's sorption properties. in Kratki izvodi radova ; Knjiga radova / 58. savetovanje Srpskog hemijskog društva, Beograd, 9. i 10. jun 2022. godine
Beograd : Srpsko hemijsko društvo., 212-215.
https://hdl.handle.net/21.15107/rcub_technorep_6574

Ivanovska AM, Branković ID, Milošević MD, Kostić MM, Svirčev ZB. Adsorption of Congo Red as an indicator for the oxidized jute fabric's sorption properties. in Kratki izvodi radova ; Knjiga radova / 58. savetovanje Srpskog hemijskog društva, Beograd, 9. i 10. jun 2022. godine. 2022;:212-215.
https://hdl.handle.net/21.15107/rcub_technorep_6574 .

Ivanovska, Aleksandra M., Branković, Ivana D., Milošević, Marija D., Kostić, Mirjana M., Svirčev, Zorica B., "Adsorption of Congo Red as an indicator for the oxidized jute fabric's sorption properties" in Kratki izvodi radova ; Knjiga radova / 58. savetovanje Srpskog hemijskog društva, Beograd, 9. i 10. jun 2022. godine (2022):212-215,
https://hdl.handle.net/21.15107/rcub_technorep_6574 .