TY  - JOUR
AU  - Glišić, Dragomir
AU  - Radović, Nenad
AU  - Drobnjak, Đorđe
AU  - Fadel, Abdunnaser
PY  - 2014
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/2799
AB  - Cleavage fracture of the medium carbon V-microalloyed steel with structure consisting of acicular ferrite, pearlite and grain boundary ferrite has been investigated by means of four-point bending of the notched samples at -196 degrees C. It was found that cleavage fracture initiation has not been related to the coarse second phase particles cracking. Calculated values of the effective surface energy of 49 J/m(2) and critical cleavage fracture stress normalized by yield stress of 1.84 are in agreement with the results for the steels with ferrite-pearlite and bainite structures.
PB  - Elsevier Science Bv, Amsterdam
T2  - 20th European Conference on Fracture
T1  - Critical stress for cleavage fracture in continuously cooled medium carbon V-microalloyed steel
EP  - 1231
SP  - 1226
VL  - 3
DO  - 10.1016/j.mspro.2014.06.199
ER  - 

@article{
author = "Glišić, Dragomir and Radović, Nenad and Drobnjak, Đorđe and Fadel, Abdunnaser",
year = "2014",
abstract = "Cleavage fracture of the medium carbon V-microalloyed steel with structure consisting of acicular ferrite, pearlite and grain boundary ferrite has been investigated by means of four-point bending of the notched samples at -196 degrees C. It was found that cleavage fracture initiation has not been related to the coarse second phase particles cracking. Calculated values of the effective surface energy of 49 J/m(2) and critical cleavage fracture stress normalized by yield stress of 1.84 are in agreement with the results for the steels with ferrite-pearlite and bainite structures.",
publisher = "Elsevier Science Bv, Amsterdam",
journal = "20th European Conference on Fracture",
title = "Critical stress for cleavage fracture in continuously cooled medium carbon V-microalloyed steel",
pages = "1231-1226",
volume = "3",
doi = "10.1016/j.mspro.2014.06.199"
}

Glišić, D., Radović, N., Drobnjak, Đ.,& Fadel, A.. (2014). Critical stress for cleavage fracture in continuously cooled medium carbon V-microalloyed steel. in 20th European Conference on Fracture
Elsevier Science Bv, Amsterdam., 3, 1226-1231.
https://doi.org/10.1016/j.mspro.2014.06.199

Glišić D, Radović N, Drobnjak Đ, Fadel A. Critical stress for cleavage fracture in continuously cooled medium carbon V-microalloyed steel. in 20th European Conference on Fracture. 2014;3:1226-1231.
doi:10.1016/j.mspro.2014.06.199 .

Glišić, Dragomir, Radović, Nenad, Drobnjak, Đorđe, Fadel, Abdunnaser, "Critical stress for cleavage fracture in continuously cooled medium carbon V-microalloyed steel" in 20th European Conference on Fracture, 3 (2014):1226-1231,
https://doi.org/10.1016/j.mspro.2014.06.199 . .

TY  - JOUR
AU  - Glišić, Dragomir
AU  - Fadel, Abdunnaser
AU  - Radović, Nenad
AU  - Drobnjak, Đorđe
AU  - Zrilić, Milorad
PY  - 2013
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/2338
AB  - The aim of this work was to establish the deformation behavior of two vanadium microalloyed medium carbon steels with different contents of carbon and titanium by tensile testing at 77 K. Samples were reheated at 1250°C for 30 min and continuously cooled in still air. Beside acicular ferrite as the dominant morphology in both microstructures, the steel with lower content of carbon and negligible amount of titanium contains considerable fraction of grain boundary ferrite and pearlite. It was found that Ti-free steel exhibits a higher strain hardening rate and significantly lower elongation at 77 K than the fully acicular ferrite steel. The difference in tensile behavior at 77 K of the two steels has been associated with the influence of the pearlite, together with higher dislocation density of acicular ferrite.
AB  - Čelici mikrolegirani vanadijumom i titanom razvijani su sa ciljem da zamene kaljene i otpuštene srednjeugljenične čelike. Iako ove čelike karakteriše dobra kombinacija čvrstoće i žilavosti, s druge strane zahtevaju naknadnu termičku obradu, koja značajno povećava troškove proizvodnje. Tehnologija dobijanja kontinuirano hlađenih čelika treba da obezbedi mikrostrukturu zahtevanih osobina posle hlađenja na vazduhu. Iz tog razloga je ovim čelicima promenjen sastav, a dobre osobine se obezbeđuju prisustvom acikularnog ferita. Acikularni ferit karakteriše nukleacija unutar prethodnog austenitnog zrna i velika razlika u kristalografskoj orijentaciji pojedinih zrna, odnosno feritnih pločica. Ova isprepletana struktura obezbeđuje povećan otpor kretanju prskotine i žilavost koja je na nivou žilavosti kod tradicionalnih kaljenih i otpuštanih čelika. U radu su ispitivana dva kontinuirano hlađena mikrolegirana čelika sa dodatkom vanadijuma. Struktura čelika bez titana i sa manjim sadržajem ugljenika ('A19') sastoji se od kontinuirane mreže proeutektoidnog ferita uz koji se izdvojio perlit, za kojim sledi acikularni ferit izdvojen unutar nekadašnjeg austenitnog zrna. Struktura čelika sa titanom i većim sadržajem ugljenika ('B22') sastoji se gotovo u potpunosti od acikularnog ferita. Deformaciono ponašanje na 77 K ispitivano je jednoosnim zatezanjem. Ukupno izduženje uzoraka čelika B22 znatno je veće nego kod čelika A19 (10 u odnosu na 5%). Čelik B22 takođe poseduje veću granicu tečenja i zateznu čvrstoću, što je razumljivo s obzirom na veći sadržaj ugljenika. Značajna razlika u duktilnosti na temperaturi tečnog azota u vezi je sa prisustvom perlita kod čelika A19, u odnosu na strukturu acikularnog ferita kod čelika B22. Brzina deformacionog ojačavanja se povećava sa povećanjem udela perlita u strukturi, čime deformacija postaje otežana, dok istovremeno konkurentni proces nastajanja mikroprskotina na krtim cementitnim lamelama ili česticama sekundarnih faza, brzo dovodi do krtog loma na 77 K. S druge strane, acikularni ferit karakteriše povećana gustina dislokacija, što se manifestuje smanjenjem brzine deformacionog ojačavanja, a time i povećanim kapacitetom deformacionog ojačavanja i većim izduženjem kod čelika B22.
PB  - Association of Chemical Engineers of Serbia
T2  - Hemijska industrija
T1  - Deformation behaviour of two continuously cooled vanadium microalloyed steels at liquid nitrogen temperature
T1  - Deformaciono ponašanje dva kontinuirano hlađena vanadijum mikrolegirana čelika na temperaturi tečnog azota
EP  - 988
IS  - 6
SP  - 981
VL  - 67
DO  - 10.2298/HEMIND121214015G
ER  - 

@article{
author = "Glišić, Dragomir and Fadel, Abdunnaser and Radović, Nenad and Drobnjak, Đorđe and Zrilić, Milorad",
year = "2013",
abstract = "The aim of this work was to establish the deformation behavior of two vanadium microalloyed medium carbon steels with different contents of carbon and titanium by tensile testing at 77 K. Samples were reheated at 1250°C for 30 min and continuously cooled in still air. Beside acicular ferrite as the dominant morphology in both microstructures, the steel with lower content of carbon and negligible amount of titanium contains considerable fraction of grain boundary ferrite and pearlite. It was found that Ti-free steel exhibits a higher strain hardening rate and significantly lower elongation at 77 K than the fully acicular ferrite steel. The difference in tensile behavior at 77 K of the two steels has been associated with the influence of the pearlite, together with higher dislocation density of acicular ferrite., Čelici mikrolegirani vanadijumom i titanom razvijani su sa ciljem da zamene kaljene i otpuštene srednjeugljenične čelike. Iako ove čelike karakteriše dobra kombinacija čvrstoće i žilavosti, s druge strane zahtevaju naknadnu termičku obradu, koja značajno povećava troškove proizvodnje. Tehnologija dobijanja kontinuirano hlađenih čelika treba da obezbedi mikrostrukturu zahtevanih osobina posle hlađenja na vazduhu. Iz tog razloga je ovim čelicima promenjen sastav, a dobre osobine se obezbeđuju prisustvom acikularnog ferita. Acikularni ferit karakteriše nukleacija unutar prethodnog austenitnog zrna i velika razlika u kristalografskoj orijentaciji pojedinih zrna, odnosno feritnih pločica. Ova isprepletana struktura obezbeđuje povećan otpor kretanju prskotine i žilavost koja je na nivou žilavosti kod tradicionalnih kaljenih i otpuštanih čelika. U radu su ispitivana dva kontinuirano hlađena mikrolegirana čelika sa dodatkom vanadijuma. Struktura čelika bez titana i sa manjim sadržajem ugljenika ('A19') sastoji se od kontinuirane mreže proeutektoidnog ferita uz koji se izdvojio perlit, za kojim sledi acikularni ferit izdvojen unutar nekadašnjeg austenitnog zrna. Struktura čelika sa titanom i većim sadržajem ugljenika ('B22') sastoji se gotovo u potpunosti od acikularnog ferita. Deformaciono ponašanje na 77 K ispitivano je jednoosnim zatezanjem. Ukupno izduženje uzoraka čelika B22 znatno je veće nego kod čelika A19 (10 u odnosu na 5%). Čelik B22 takođe poseduje veću granicu tečenja i zateznu čvrstoću, što je razumljivo s obzirom na veći sadržaj ugljenika. Značajna razlika u duktilnosti na temperaturi tečnog azota u vezi je sa prisustvom perlita kod čelika A19, u odnosu na strukturu acikularnog ferita kod čelika B22. Brzina deformacionog ojačavanja se povećava sa povećanjem udela perlita u strukturi, čime deformacija postaje otežana, dok istovremeno konkurentni proces nastajanja mikroprskotina na krtim cementitnim lamelama ili česticama sekundarnih faza, brzo dovodi do krtog loma na 77 K. S druge strane, acikularni ferit karakteriše povećana gustina dislokacija, što se manifestuje smanjenjem brzine deformacionog ojačavanja, a time i povećanim kapacitetom deformacionog ojačavanja i većim izduženjem kod čelika B22.",
publisher = "Association of Chemical Engineers of Serbia",
journal = "Hemijska industrija",
title = "Deformation behaviour of two continuously cooled vanadium microalloyed steels at liquid nitrogen temperature, Deformaciono ponašanje dva kontinuirano hlađena vanadijum mikrolegirana čelika na temperaturi tečnog azota",
pages = "988-981",
number = "6",
volume = "67",
doi = "10.2298/HEMIND121214015G"
}

Glišić, D., Fadel, A., Radović, N., Drobnjak, Đ.,& Zrilić, M.. (2013). Deformation behaviour of two continuously cooled vanadium microalloyed steels at liquid nitrogen temperature. in Hemijska industrija
Association of Chemical Engineers of Serbia., 67(6), 981-988.
https://doi.org/10.2298/HEMIND121214015G

Glišić D, Fadel A, Radović N, Drobnjak Đ, Zrilić M. Deformation behaviour of two continuously cooled vanadium microalloyed steels at liquid nitrogen temperature. in Hemijska industrija. 2013;67(6):981-988.
doi:10.2298/HEMIND121214015G .

Glišić, Dragomir, Fadel, Abdunnaser, Radović, Nenad, Drobnjak, Đorđe, Zrilić, Milorad, "Deformation behaviour of two continuously cooled vanadium microalloyed steels at liquid nitrogen temperature" in Hemijska industrija, 67, no. 6 (2013):981-988,
https://doi.org/10.2298/HEMIND121214015G . .