TY  - JOUR
AU  - Musraty, Walid
AU  - Međo, Bojan
AU  - Gubeljak, Nenad
AU  - Likeb, A.
AU  - Cvijović-Alagić, Ivana
AU  - Sedmak, Aleksandar
AU  - Rakin, Marko
PY  - 2017
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3734
AB  - Integrity of pipes is typically assessed by testing fracture mechanics specimens, such as compact tensile (CT) or single-edge notched bending (SENB). However, for some pipe dimensions it is not easy or possible to fabricate a specimen conforming to the requirements of standard procedures. A new type of specimen is proposed recently, which can be advantageous for relatively small pipe diameters and axial defects - the pipe ring notch bend specimen - PRNB. In this work, criteria for failure by ductile fracture of PRNB specimens are determined experimentally and by application of micromechanical analysis. The influence of size of the specimen, as well as size and shape of the stress concentrator, is analysed. The results of this study, along with previous authors' results, lead to the conclusion that the pipe ring specimens can be applied in integrity assessment of pipes with defects. Also, the benefits of their application include much simpler fabrication and the same material history as the pipe itself.
PB  - Pergamon-Elsevier Science Ltd, Oxford
T2  - Engineering Fracture Mechanics
T1  - Ductile fracture of pipe-ring notched bend specimens - Micromechanical analysis
EP  - 261
SP  - 247
VL  - 175
DO  - 10.1016/j.engfracmech.2017.01.022
ER  - 

@article{
author = "Musraty, Walid and Međo, Bojan and Gubeljak, Nenad and Likeb, A. and Cvijović-Alagić, Ivana and Sedmak, Aleksandar and Rakin, Marko",
year = "2017",
abstract = "Integrity of pipes is typically assessed by testing fracture mechanics specimens, such as compact tensile (CT) or single-edge notched bending (SENB). However, for some pipe dimensions it is not easy or possible to fabricate a specimen conforming to the requirements of standard procedures. A new type of specimen is proposed recently, which can be advantageous for relatively small pipe diameters and axial defects - the pipe ring notch bend specimen - PRNB. In this work, criteria for failure by ductile fracture of PRNB specimens are determined experimentally and by application of micromechanical analysis. The influence of size of the specimen, as well as size and shape of the stress concentrator, is analysed. The results of this study, along with previous authors' results, lead to the conclusion that the pipe ring specimens can be applied in integrity assessment of pipes with defects. Also, the benefits of their application include much simpler fabrication and the same material history as the pipe itself.",
publisher = "Pergamon-Elsevier Science Ltd, Oxford",
journal = "Engineering Fracture Mechanics",
title = "Ductile fracture of pipe-ring notched bend specimens - Micromechanical analysis",
pages = "261-247",
volume = "175",
doi = "10.1016/j.engfracmech.2017.01.022"
}

Musraty, W., Međo, B., Gubeljak, N., Likeb, A., Cvijović-Alagić, I., Sedmak, A.,& Rakin, M.. (2017). Ductile fracture of pipe-ring notched bend specimens - Micromechanical analysis. in Engineering Fracture Mechanics
Pergamon-Elsevier Science Ltd, Oxford., 175, 247-261.
https://doi.org/10.1016/j.engfracmech.2017.01.022

Musraty W, Međo B, Gubeljak N, Likeb A, Cvijović-Alagić I, Sedmak A, Rakin M. Ductile fracture of pipe-ring notched bend specimens - Micromechanical analysis. in Engineering Fracture Mechanics. 2017;175:247-261.
doi:10.1016/j.engfracmech.2017.01.022 .

Musraty, Walid, Međo, Bojan, Gubeljak, Nenad, Likeb, A., Cvijović-Alagić, Ivana, Sedmak, Aleksandar, Rakin, Marko, "Ductile fracture of pipe-ring notched bend specimens - Micromechanical analysis" in Engineering Fracture Mechanics, 175 (2017):247-261,
https://doi.org/10.1016/j.engfracmech.2017.01.022 . .

TY  - JOUR
AU  - Tomsić, Brigita
AU  - Vasiljević, Jelena
AU  - Simončič, Barbara
AU  - Radoičić, Marija B.
AU  - Radetić, Maja
PY  - 2017
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3543
AB  - This study discusses the effect of corona pre-treatment at atmospheric pressure and subsequent loading of colloidal TiO2 nanoparticles on the biodegradation behavior of cotton fabric. Biodegradation performance of the control and finished samples was evaluated by standard soil burial tests in predetermined periods of 3, 9 and 18 days. Color and breaking strength measurements were utilized for assessment of biodegradation progress. Morphological and chemical changes induced by biodegradation were analysed by SEM and FT-IR analyses, respectively. Colorimetric, morphological and chemical changes induced by the biodegradation process were slightly less prominent on corona pre-treated cotton fabric impregnated with TiO2 nanoparticles compared to corona treated and control cotton fabric. Although the breaking strength of all samples significantly decreased after 18 days of soil burial, this decline was the least evident on the sample impregnated with TiO2 nanoparticles. However, taking into account the extent of these differences, the influence of TiO2 nanoparticles on biodegradation rate of cotton fabric, which underwent a combined treatment corona/impregnation with TiO2 nanoparticles, could be considered as insignificant. These results confirm that chemical modification of cotton fabrics with plasma and subsequent loading of TiO2 still maintained sustainability of cellulose fibres.
PB  - Springer, Dordrecht
T2  - Cellulose
T1  - The influence of corona treatment and impregnation with colloidal TiO2 nanoparticles on biodegradability of cotton fabric
EP  - 4545
IS  - 10
SP  - 4533
VL  - 24
DO  - 10.1007/s10570-017-1415-6
ER  - 

@article{
author = "Tomsić, Brigita and Vasiljević, Jelena and Simončič, Barbara and Radoičić, Marija B. and Radetić, Maja",
year = "2017",
abstract = "This study discusses the effect of corona pre-treatment at atmospheric pressure and subsequent loading of colloidal TiO2 nanoparticles on the biodegradation behavior of cotton fabric. Biodegradation performance of the control and finished samples was evaluated by standard soil burial tests in predetermined periods of 3, 9 and 18 days. Color and breaking strength measurements were utilized for assessment of biodegradation progress. Morphological and chemical changes induced by biodegradation were analysed by SEM and FT-IR analyses, respectively. Colorimetric, morphological and chemical changes induced by the biodegradation process were slightly less prominent on corona pre-treated cotton fabric impregnated with TiO2 nanoparticles compared to corona treated and control cotton fabric. Although the breaking strength of all samples significantly decreased after 18 days of soil burial, this decline was the least evident on the sample impregnated with TiO2 nanoparticles. However, taking into account the extent of these differences, the influence of TiO2 nanoparticles on biodegradation rate of cotton fabric, which underwent a combined treatment corona/impregnation with TiO2 nanoparticles, could be considered as insignificant. These results confirm that chemical modification of cotton fabrics with plasma and subsequent loading of TiO2 still maintained sustainability of cellulose fibres.",
publisher = "Springer, Dordrecht",
journal = "Cellulose",
title = "The influence of corona treatment and impregnation with colloidal TiO2 nanoparticles on biodegradability of cotton fabric",
pages = "4545-4533",
number = "10",
volume = "24",
doi = "10.1007/s10570-017-1415-6"
}

Tomsić, B., Vasiljević, J., Simončič, B., Radoičić, M. B.,& Radetić, M.. (2017). The influence of corona treatment and impregnation with colloidal TiO2 nanoparticles on biodegradability of cotton fabric. in Cellulose
Springer, Dordrecht., 24(10), 4533-4545.
https://doi.org/10.1007/s10570-017-1415-6

Tomsić B, Vasiljević J, Simončič B, Radoičić MB, Radetić M. The influence of corona treatment and impregnation with colloidal TiO2 nanoparticles on biodegradability of cotton fabric. in Cellulose. 2017;24(10):4533-4545.
doi:10.1007/s10570-017-1415-6 .

Tomsić, Brigita, Vasiljević, Jelena, Simončič, Barbara, Radoičić, Marija B., Radetić, Maja, "The influence of corona treatment and impregnation with colloidal TiO2 nanoparticles on biodegradability of cotton fabric" in Cellulose, 24, no. 10 (2017):4533-4545,
https://doi.org/10.1007/s10570-017-1415-6 . .