TY  - JOUR
AU  - Veljović, Đorđe
AU  - Jokić, Bojan
AU  - Janković-Častvan, Ivona
AU  - Smičiklas, Ivana D.
AU  - Petrović, Rada
AU  - Janaćković, Đorđe
PY  - 2007
UR  - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/1021
AB  - The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained.
PB  - Trans Tech Publications Ltd, Durnten-Zurich
T2  - Key Engineering Materials
T1  - Sintering behaviour of nanosized HAP powder
EP  - 262
SP  - 259
VL  - 330-332 I
UR  - https://hdl.handle.net/21.15107/rcub_technorep_1021
ER  - 

@article{
author = "Veljović, Đorđe and Jokić, Bojan and Janković-Častvan, Ivona and Smičiklas, Ivana D. and Petrović, Rada and Janaćković, Đorđe",
year = "2007",
abstract = "The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained.",
publisher = "Trans Tech Publications Ltd, Durnten-Zurich",
journal = "Key Engineering Materials",
title = "Sintering behaviour of nanosized HAP powder",
pages = "262-259",
volume = "330-332 I",
url = "https://hdl.handle.net/21.15107/rcub_technorep_1021"
}

Veljović, Đ., Jokić, B., Janković-Častvan, I., Smičiklas, I. D., Petrović, R.,& Janaćković, Đ.. (2007). Sintering behaviour of nanosized HAP powder. in Key Engineering Materials
Trans Tech Publications Ltd, Durnten-Zurich., 330-332 I, 259-262.
https://hdl.handle.net/21.15107/rcub_technorep_1021

Veljović Đ, Jokić B, Janković-Častvan I, Smičiklas ID, Petrović R, Janaćković Đ. Sintering behaviour of nanosized HAP powder. in Key Engineering Materials. 2007;330-332 I:259-262.
https://hdl.handle.net/21.15107/rcub_technorep_1021 .

Veljović, Đorđe, Jokić, Bojan, Janković-Častvan, Ivona, Smičiklas, Ivana D., Petrović, Rada, Janaćković, Đorđe, "Sintering behaviour of nanosized HAP powder" in Key Engineering Materials, 330-332 I (2007):259-262,
https://hdl.handle.net/21.15107/rcub_technorep_1021 .