Investigation of dynamic young modulus during thermal stability testing of the refractory material / Određivanje dinamičkog jungovog modula elastičnosti tokom ispitivanja termostabilnosti vatrostalnog materijala
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Thermal stability of the refractory material with the content of 42 % Al2O3 was investigated. Water quench test (JUS.B.D8.319.) was applied. Photographs of the samples before cycling, and after some number of cycles were ...
Laboratory investigation of cavitation resistance of materials: Modified ultrasonically induced cavitation test method / Laboratorijsko istraživanje kavitacione otpornosti materijala - modificirana ultrazvučna metoda
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Cavitation erosion represents an actual problem in machines, whose components such as propellers, blades of hydraulic pumps and turbines, are exposed to high-speed flow of liquid. Research exhibited that hydraulic machinery ...
Structure and kinetics of internal oxidation in Ag-Sn alloys / Struktura i kinetika interne oksidacije Ag-Sn legura
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Internal oxidation in Ag-Sn-In-Te and Ag-Sn-Cu-Bi alloys was tested. micro structures of casted and homogenized samples, as well as after internal oxidation were followed by optical microscopy. The structure of Ag-Sn-Cu-Bi ...
Hydrometallurgical process for extraction of metals from electronic waste, Part I: Material characterization and process option selection
(Savez inženjera metalurgije Srbije, Beograd, 2009)
Used electronic equipment became one of the fastest growing waste streams in the world. In the past two decades recycling of printed circuit boards (PCBs) has been based on pyrometallurgy, highly polluting recycling ...
Experimental design approach regarding kinetics of high pressure leaching processes / Dizajniranje eksperimenata u pogledu na kinetiku luženja pri visokim pritiscima
(Savez inženjera metalurgije Srbije, Beograd, 2003)
Kinetics of high pressure leaching of nickel latente ore "Rudjinci", Serbia was studied in this work. The following parameters: temperature, acid to ore ratio, stirring speed, and time were optimized in order to obtain the ...
The influence of the solidification rate on the interface shape and distribution of solute
(Savez inženjera metalurgije Srbije, Beograd, 2002)
In this paper investigation of the influence of the solidification conditions on the interface shape and distribution of solute during the solidification of AI-Cu alloy by vertical Bridgman method were investigated. The ...
On the Al-Mg alloy sheets for automotive application: Problems and solutions
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Aluminium alloys suitable for automotive application were reviewed briefly as well as the reasons for the future wider application of Al-Mg type alloys. Basic problems related to the limited consumption of Al-Mg type alloy ...
The influence of the interface shape on the plane-to-cellular-to-dendritic transition in superalloy based of nickel
(Savez inženjera metalurgije Srbije, Beograd, 2004)
In this paper investigation of the influence of the crystallization conditions on the interface shape during the solidification of Ni-based Superalloy by Vertical Bridgman method were investigated. The samples were undertaken ...
A case study of global steel properties database development: Key to steel / Primer razvoja globalne baze podataka osobina čelika - key to steel
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Key to Steel is the world’s most comprehensive database of steel materials developed to provide technical information to professional users worldwide. This paper describes development process that resulted in the biggest ...
Dependence of the solid-liquid interface structure on the solidification process parameters / Zavisnost strukture granice faza tečno-čvrsto od parametara procesa očvršćavanja
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Influence of the solidification rate, temperature gradient and initial concentration of the solute on the interface shape was investigated during solidification from the melt. The dependence of the microstructure on the ...