Effects of poly(vinyl alcohol) blending with Ag/alginate solutions to form nanocomposite fibres for potential use as antibacterial wound dressings
(Royal Society Publishing, 2022)
In this work, nanocomposite fibres and microfibres based on alginate and poly(vinyl alcohol) (PVA) with silver nanoparticles (AgNPs) were produced and characterized for potential application as antibacterial wound dressings. ...
Inorganically modified particles FeAl-LDH"SiO2 as reinforcement in poly (methyl) methacrylate matrix composite
(Royal Society Open Science, 2021)
Silica particles were obtained from rice husk to which layered double hydroxide particles were deposited (weight ratio 1 : 1). Fe2+-Al3+ layered double hydroxides (FeAl-LDH) were synthesized by co-precipitation with ratios ...
CIRCULAR ECONOMY IMPLEMENTATION IN THE DEVELOPMENT OF FIRE-RETARDANT MATERIALS USED IN CONSTRUCTION, INDUSTRY, AND GENERAL-PURPOSE PRODUCTS
(Association of Metallurgical Engineers of Serbia, 2022)
During a fire, passive fire protection systems are designed to prevent the spread of flames, smoke, and toxic gases. The new fire-retardant (FR) material, used for passive fire protection, is created by combining copolymers ...
Comparative Study of the Microstructure and Properties of Cast-Fabricated and 3D-Printed Laser-Sintered Co–Cr Alloys for Removable Partial Denture Frameworks
(MDPI, 2023)
Since additive technologies in dentistry are gradually replacing metal casting technology, it is necessary to evaluate new dental constructions intended for the development of removable partial denture frameworks. The aim ...
Synthesis and characterization of semi-interpenetrating networks of chitosan and poly(N-vinyl-2-pyrrolidone) / Sinteza i karakterizacija semi-interpenetrirajućih mreža hitozana i poli(N-vinil-2-pirolidona)
(Association of Chemical Engineers of Serbia, 2010)
Semi-interpenetrating networks (semi-IPNs) based on chitosan and poly(N-vinyl-2-pyrrolidone) were prepared in order to achieve better mechanical properties. The samples were characterized by FTIR, SEM, DMA analysis and the ...
Age hardening potential of an Al-4.6 wt.% Mg alloy with Cu addition
(Belgrade : Institute of Technical Sciences of SASA, 2010)
The ageing behavior of an Al-4.6Mg-0.54Cu (in wt.%) alloy was studied after: (i) solution
treatment for 1h at 530°C, and (ii) annealing at 280°C for 3h. Both groups of the heat treated
specimens underwent further ...
Synthesis, Characterization and Application of Biobased Unsaturated Polyester Resin Reinforced with Unmodified/Modified Biosilica Nanoparticles
(MDPI, 2023)
This paper presents sustainable technology for environmentally friendly composite production. Biobased unsaturated polyester resin (b-UPR), synthesized from waste polyethylene terephthalate (PET) glycosylate and renewable ...
Quality of Cotton and cotton/elastane Single Jersey Knitted Fabrics before and after Softening and in Situ Synthesis of Cu-based Nanoparticles
(Taylor and Francis Ltd., 2022)
The quality of cotton and cotton/elastane single jersey knitted fabrics before and after softening was evaluated through their mechanical properties, pilling, and volume electrical resistivity. Elastane-containing fabrics ...
Mechanical properties of two Al-Mg alloys manufactured by accumulative roll bonding (ARB) process
(Belgrade : Association of Metallurgical Engineers of Serbia (AMES), 2017)
The influence of alloying on the mechanical properties of AA5083 type Al-Mg
alloy sheets produced by accumulative roll bonding (ARB) process was studied.
Two investigated Al-Mg alloys: commercial AA5083 alloy with 4.2% ...
Influence of an accumulative roll bonding (ARB) process on the properties of AA5083 Al-Mg alloy sheets
(Association of Metallurgical Engineers of Serbia AMES, 2014)
In this study, fully annealed AA5083 type alloy sheets with 1 mm in thickness
were processed by accumulative roll bonding (ARB) at room temperature, up to 6 ARB
cycles. It was found that microstructure was refined and ...