Kinetic analysis of hydrogen evolution at Ni-Mo alloy electrodes
(Elsevier Science Ltd, 2000)
The hydrogen evolution reaction (HER) on Ni, Mo and MoNi intermetallic compound was investigated with ac impedance and dc polarization measurements in 1.0 mol dm-3 NaOH solution at 25 °C. The rate constants of the forward ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
The influence of the aging time of RuO2 and TiO2 sols on the electrochemical properties and behavior for the chlorine evolution reaction of activated titanium anodes obtained by the sol-gel procedure
(Elsevier, 2000)
The influence of the aging time of RuO2 and TiO2 sols used for the preparation of (40% RuO2+60% TiO2)/Ti anodes by the sol-gel procedure on the electrochemical properties and behavior for the chlorine evolution reaction ...
Methanol oxidation on an ink type electrode using Pt supported on high area carbons
(Pergamon-Elsevier Science Ltd, Oxford, 2001)
Methanol oxidation was investigated on the following Pt catalysts: bare Pt electrode, Pt covered by nafion (R) film, and pt catalysts supported on high area carbons in the form of an ink. The reaction was carried out using ...
HCOOH oxidation on thin Pd layers on Au: Self-poisoning by the subsequent reaction of the reaction product
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The oxidation of HCOOH has been investigated on thin Pd layers ranging from 1 to 17 ML equivalents electrodeposited on polycrystalline Au substrate (Pd"Au). The results are compared to those on Pd black. Potentiodynamic ...
Synthesis and characterization of MoOx-Pt/C and TiOx-Pt/C nano-catalysts for oxygen reduction
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The oxygen reduction reaction (ORR) was studied at carbon supported MoOx-Pt/C and TiOx-Pt nanocatalysts in 0.5 mol dm(-3) HClO4 solution, at 25 degrees C. The MoOx-Pt/C and TiOx-Pt/C catalysts were prepared by the polyole ...
Hydrogen evolution in acid solution at Pd electrodeposited onto Ti2AlC
(Pergamon-Elsevier Science Ltd, Oxford, 2017)
The hydrogen evolution reaction (HER) was studied in 0.5 M H2SO4 at 25 degrees C on Pd electrodeposited onto Ti2AlC substrate, as an excellent substrate due to its high conductivity and high stability in concentrated ...
Incorporation of Pt, Ru and Pt-Ru nanoparticles into ordered mesoporous carbons for efficient oxygen reduction reaction in alkaline media
(Electrochimica Acta, 2015)
Ordered mesoporous carbon, volume-doped up to 3w.% with Pt, Ru and Pt-Ru nanoparticles was synthesized by evaporation-induced self-assembly method, under acidic conditions. The content of incorporated metal was determined ...
Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
In this work the hydrogen evolution reaction (HER) at Ni-Sn alloy coatings, deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) SnCl2 + 0.3 mol dm(-3) NiCl2 in the pyrophosphate-glycine ...