The influence of the sintering regime on the stability of the SmCo5 phase
Само за регистроване кориснике
1997
Аутори
Talijan, NadeždaMilutinović-Nikolić, Aleksandra
Jančić, Radmila
Petrović-Prelević, I
Stajić-Trošić, Jasna
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The purpose of this investigation was to establish the correlation between the sintering conditions (temperature and time) and the stability of the SmCo5 phase, expressed by the intensity of its most important diffraction peak. The sintering and heat treatment was performed under a vacuum of 150 Pa. Sintering was investigated in the temperature interval from 1100 to 1180 degrees C, for sintering times of 30, 45 and 60 min, while the temperature and duration of the heat treatment were kept constant. The content of the SmCo5 phase, as the carrier of the magnetic properties, was observed by X-ray diffraction analysis of the polycrystalline specimens. It was established that there is a dependence of the intensity of the diffraction peak, which corresponds to the (111) plane of the SmCo5 phase, on the sintering time and temperature. A regression model was obtained that showed the intensity of the diffraction peak to be dependent upon squares of both the sintering time and temperature.
Кључне речи:
sintering / stability of SmCo5 phase / X-ray analysis / modelИзвор:
Materials Letters, 1997, 32, 2-3, 85-89Издавач:
- Elsevier, Amsterdam
DOI: 10.1016/S0167-577X(97)00017-7
ISSN: 0167-577X
WoS: A1997XV87700007
Scopus: 2-s2.0-0031209973
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Talijan, Nadežda AU - Milutinović-Nikolić, Aleksandra AU - Jančić, Radmila AU - Petrović-Prelević, I AU - Stajić-Trošić, Jasna PY - 1997 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/125 AB - The purpose of this investigation was to establish the correlation between the sintering conditions (temperature and time) and the stability of the SmCo5 phase, expressed by the intensity of its most important diffraction peak. The sintering and heat treatment was performed under a vacuum of 150 Pa. Sintering was investigated in the temperature interval from 1100 to 1180 degrees C, for sintering times of 30, 45 and 60 min, while the temperature and duration of the heat treatment were kept constant. The content of the SmCo5 phase, as the carrier of the magnetic properties, was observed by X-ray diffraction analysis of the polycrystalline specimens. It was established that there is a dependence of the intensity of the diffraction peak, which corresponds to the (111) plane of the SmCo5 phase, on the sintering time and temperature. A regression model was obtained that showed the intensity of the diffraction peak to be dependent upon squares of both the sintering time and temperature. PB - Elsevier, Amsterdam T2 - Materials Letters T1 - The influence of the sintering regime on the stability of the SmCo5 phase EP - 89 IS - 2-3 SP - 85 VL - 32 DO - 10.1016/S0167-577X(97)00017-7 ER -
@article{ author = "Talijan, Nadežda and Milutinović-Nikolić, Aleksandra and Jančić, Radmila and Petrović-Prelević, I and Stajić-Trošić, Jasna", year = "1997", abstract = "The purpose of this investigation was to establish the correlation between the sintering conditions (temperature and time) and the stability of the SmCo5 phase, expressed by the intensity of its most important diffraction peak. The sintering and heat treatment was performed under a vacuum of 150 Pa. Sintering was investigated in the temperature interval from 1100 to 1180 degrees C, for sintering times of 30, 45 and 60 min, while the temperature and duration of the heat treatment were kept constant. The content of the SmCo5 phase, as the carrier of the magnetic properties, was observed by X-ray diffraction analysis of the polycrystalline specimens. It was established that there is a dependence of the intensity of the diffraction peak, which corresponds to the (111) plane of the SmCo5 phase, on the sintering time and temperature. A regression model was obtained that showed the intensity of the diffraction peak to be dependent upon squares of both the sintering time and temperature.", publisher = "Elsevier, Amsterdam", journal = "Materials Letters", title = "The influence of the sintering regime on the stability of the SmCo5 phase", pages = "89-85", number = "2-3", volume = "32", doi = "10.1016/S0167-577X(97)00017-7" }
Talijan, N., Milutinović-Nikolić, A., Jančić, R., Petrović-Prelević, I.,& Stajić-Trošić, J.. (1997). The influence of the sintering regime on the stability of the SmCo5 phase. in Materials Letters Elsevier, Amsterdam., 32(2-3), 85-89. https://doi.org/10.1016/S0167-577X(97)00017-7
Talijan N, Milutinović-Nikolić A, Jančić R, Petrović-Prelević I, Stajić-Trošić J. The influence of the sintering regime on the stability of the SmCo5 phase. in Materials Letters. 1997;32(2-3):85-89. doi:10.1016/S0167-577X(97)00017-7 .
Talijan, Nadežda, Milutinović-Nikolić, Aleksandra, Jančić, Radmila, Petrović-Prelević, I, Stajić-Trošić, Jasna, "The influence of the sintering regime on the stability of the SmCo5 phase" in Materials Letters, 32, no. 2-3 (1997):85-89, https://doi.org/10.1016/S0167-577X(97)00017-7 . .