Microstructure evolution and mechanical properties degradation of HPNB alloy after an eleven-year service / Mikrostrukturni razvoj i degradacija mehaničkih svojstava legure HPNB posle jedanaest godina eksploatacije
(Society for Structural Integrity and Life (DIVK), 2022)
In this work, the heat-resistant cast steel HP40Nb alloy, produced in the form of a centrifugally cast tube, which failed after 11.4 years service is investigated. The microstructure is examined using a scanning electron ...
Corrosion resistance of welded pipe in oil wells / Otpornost na koroziju zavarenih cevi u naftnim bušotinama
(Engineering Society for Corrosion, Belgrade, Serbia, 2013)
Steel pipes in oil and gas wells are continuously exposed to the process of corrosion-assisted elevated temperatures and pressures prevailing in the interior of the tube. Corrosion can lead to significant reduction of ...
Strength design calculation of a horizontal pressure vessel / Kontrolni proračun čvrstoće horizontalne posude pod pritiskom
(Society for Structural Integrity and Life, Institute for Material Testing, 2013)
Standards SRPS M.E2.250-262 for calculation of pres-sure vessels have been replaced by SRPS EN 13445-3. This means that calculations of new equipment and check calculations of equipment in service are subjected to ordinance ...
An overview of application of micromechanical models in ductile fracture analysis of welded joints
(Srpsko društvo za mehaniku, Beograd, 2020)
Fracture of welded joints has been an important research and industrial topic for a long time, having in mind the key role of welded joints in ensuring the safe operation and integrity of welded structures. This work ...
Influence of an accumulative roll bonding (ARB) process on the properties of AA5083 Al-Mg alloy sheets
(Association of Metallurgical Engineers of Serbia AMES, 2014)
In this study, fully annealed AA5083 type alloy sheets with 1 mm in thickness
were processed by accumulative roll bonding (ARB) at room temperature, up to 6 ARB
cycles. It was found that microstructure was refined and ...
Effect of the pH of artificial saliva on ion release from commercially pure titanium / Uticaj pH vrednosti veštačke pljuvačke na otpuštanje jona iz komercijalno čistog titana
(Faculty of Technology, Novi Sad, 2013)
Due to their excellent characteristics, such as chemical inertness, mechanical resistance, low Young's modulus, high corrosion resistance, and outstanding biocompatibility, titanium and its alloys are the most used metallic ...
Influence of defects on limit loads and integrity of the pipeline at hydropower plant 'Pirot'
(Society for Structural Integrity and Life, Institute for Material Testing, 2020)
Topic of this work is the integrity assessment of the pipeline section from hydropower plant Pirot. Crack-like defect size, maximum depth, is determined based on non-destructive evaluation - the largest crack depth is taken ...
Prednosti zavarivanja trenjem sa mešanjem u odnosu na elektrolučno zavarivanje - zaštita zdravlja i životne sredine i bezbednost na radu / Advantages of friction stir welding over arc welding with respect to health and environmental protection and work safety
(Society for Structural Integrity and Life (DIVK), 2015)
U savremenoj industrijskoj proizvodnji, svaki proizvodni proces treba da bude ispitan u pogledu uticaja na životnu sredinu. Za svaku kompaniju koja investira u novi proces je od značaja pažljivo razmatranje HSE (Health, ...
Effect of corn straw pretreatment on efficiency of biogas production process: Computer simulation
(Institut za istrazivanja i projektovanja u privredi, 2020)
Anaerobic digestion is a natural process of organic material degradation by different kinds of microorganisms in the absence of oxygen. This process is used for industrial purpose to manage waste streams or to produce ...
Effect of plasma hardfacing and carbides presence on the occurrence of cracks and microcracks
(Society for Structural Integrity and Life, Institute for Material Testing, 2018)
Presented is the effect of plasma hardfacing (or just hardfacing) and carbides presence on the occurrence of cracks and microcracks in the welded layer. The reasons behind this phenomenon are analysed and explained. In ...