Određivanje otpornosti na dejstvo kavitacije uzoraka pirofilita
Determination of resistance to cavitation of pyrophyllite samples
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
U radu je ispitivana otpornost pod dejstvom kavitacije uzoraka sinterovanog pirofilita. Polazni
uzorak pirofilita iz ležišta Parsović- BiH mleven je u vibracionom mlinu na granulaciju 20μm,
presovan je i sinterovan na temperaturama (ºC): 1000; 1100; 1200. Za procenu kavitacione
otpornosti praćena je promena mase uzorka u funkciji vremena delovanja kavitacije. Primenjena je
ultrazvučna vibraciona metoda sa stacionarnim uzorkom prema standardu ASTM G32. Izračunate
su kavitacione brzine za sve uzorke, kao osnovni pokazatelj otpornosti materijala pod dejstvom
kavitacije. Promena morfologije površine uzorka sa vremenom ispitivanja praćena je primenom
skenirajuće elektronske mikroskopije. Na osnovu vrednosti kavitacione brzine i analize morfologije
oštećenja površine određena je kavitaciona otpornost ispitivanih uzoraka na bazi pirofilita. Dobijeni
rezultati ukazuju da uzorci sinterovanog pirofilita imaju zadovoljavajuću otpornost na dejstvo
kavitacije i mogu se primeniti u uslovim...a manjih kavitacionih opterećenja.
The resistance under the action of cavitation of sintered pyrophillite samples was investigated. The initial sample of pyrophillite from the Parsovic-BiH deposit was ground a vibrating mill to a granulation of 20 mμ, pressed and sintered at temperatures (⁰C): 100; 1100; 1200. To assess cavitation resistance, the change in sample mass as a function of cavitation time was monitored. The cavitation erosion test was performed using the ultrasonic vibratory cavitation test method according to the ASTM G-32 standard. Cavitation velocites were calculated for all samples, as a basic indicator of the resistance of the material under the action of cavitation. The change in the morphology of the surface with the test time was followed by scanning electron microscopy. Based on the values of cavitation velocity and analysis of the surface damage morphology, the cavitation resistance of the tested samples based on pyrophillite was determined. The obtained results indicate that the samples of sintere...d pyrophillite have satisfactory resistance to the action of cavitation and be applied in conditions of lower cavitation loads.
Кључне речи:
pirofilit / kavitaciona otpornost / gubitak mase / morfologija oštećenja / analiza slikeИзвор:
Zaštita materijala, 2021, 62, 2, 126-134Издавач:
- Inženjersko društvo za koroziju
Финансирање / пројекти:
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200023 (Институт за технологију нуклеарних и других минералних сировина - ИТНМС, Београд) (RS-MESTD-inst-2020-200023)
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200135 (Универзитет у Београду, Технолошко-металуршки факултет) (RS-MESTD-inst-2020-200135)
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Andrić, Ljubiša AU - Pavlović, Marko AU - Dojčinović, Marina AU - Radulović, Dragan PY - 2021 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/5625 AB - U radu je ispitivana otpornost pod dejstvom kavitacije uzoraka sinterovanog pirofilita. Polazni uzorak pirofilita iz ležišta Parsović- BiH mleven je u vibracionom mlinu na granulaciju 20μm, presovan je i sinterovan na temperaturama (ºC): 1000; 1100; 1200. Za procenu kavitacione otpornosti praćena je promena mase uzorka u funkciji vremena delovanja kavitacije. Primenjena je ultrazvučna vibraciona metoda sa stacionarnim uzorkom prema standardu ASTM G32. Izračunate su kavitacione brzine za sve uzorke, kao osnovni pokazatelj otpornosti materijala pod dejstvom kavitacije. Promena morfologije površine uzorka sa vremenom ispitivanja praćena je primenom skenirajuće elektronske mikroskopije. Na osnovu vrednosti kavitacione brzine i analize morfologije oštećenja površine određena je kavitaciona otpornost ispitivanih uzoraka na bazi pirofilita. Dobijeni rezultati ukazuju da uzorci sinterovanog pirofilita imaju zadovoljavajuću otpornost na dejstvo kavitacije i mogu se primeniti u uslovima manjih kavitacionih opterećenja. AB - The resistance under the action of cavitation of sintered pyrophillite samples was investigated. The initial sample of pyrophillite from the Parsovic-BiH deposit was ground a vibrating mill to a granulation of 20 mμ, pressed and sintered at temperatures (⁰C): 100; 1100; 1200. To assess cavitation resistance, the change in sample mass as a function of cavitation time was monitored. The cavitation erosion test was performed using the ultrasonic vibratory cavitation test method according to the ASTM G-32 standard. Cavitation velocites were calculated for all samples, as a basic indicator of the resistance of the material under the action of cavitation. The change in the morphology of the surface with the test time was followed by scanning electron microscopy. Based on the values of cavitation velocity and analysis of the surface damage morphology, the cavitation resistance of the tested samples based on pyrophillite was determined. The obtained results indicate that the samples of sintered pyrophillite have satisfactory resistance to the action of cavitation and be applied in conditions of lower cavitation loads. PB - Inženjersko društvo za koroziju T2 - Zaštita materijala T1 - Određivanje otpornosti na dejstvo kavitacije uzoraka pirofilita T1 - Determination of resistance to cavitation of pyrophyllite samples EP - 134 IS - 2 SP - 126 VL - 62 DO - 10.5937/zasmat2102126A ER -
@article{ author = "Andrić, Ljubiša and Pavlović, Marko and Dojčinović, Marina and Radulović, Dragan", year = "2021", abstract = "U radu je ispitivana otpornost pod dejstvom kavitacije uzoraka sinterovanog pirofilita. Polazni uzorak pirofilita iz ležišta Parsović- BiH mleven je u vibracionom mlinu na granulaciju 20μm, presovan je i sinterovan na temperaturama (ºC): 1000; 1100; 1200. Za procenu kavitacione otpornosti praćena je promena mase uzorka u funkciji vremena delovanja kavitacije. Primenjena je ultrazvučna vibraciona metoda sa stacionarnim uzorkom prema standardu ASTM G32. Izračunate su kavitacione brzine za sve uzorke, kao osnovni pokazatelj otpornosti materijala pod dejstvom kavitacije. Promena morfologije površine uzorka sa vremenom ispitivanja praćena je primenom skenirajuće elektronske mikroskopije. Na osnovu vrednosti kavitacione brzine i analize morfologije oštećenja površine određena je kavitaciona otpornost ispitivanih uzoraka na bazi pirofilita. Dobijeni rezultati ukazuju da uzorci sinterovanog pirofilita imaju zadovoljavajuću otpornost na dejstvo kavitacije i mogu se primeniti u uslovima manjih kavitacionih opterećenja., The resistance under the action of cavitation of sintered pyrophillite samples was investigated. The initial sample of pyrophillite from the Parsovic-BiH deposit was ground a vibrating mill to a granulation of 20 mμ, pressed and sintered at temperatures (⁰C): 100; 1100; 1200. To assess cavitation resistance, the change in sample mass as a function of cavitation time was monitored. The cavitation erosion test was performed using the ultrasonic vibratory cavitation test method according to the ASTM G-32 standard. Cavitation velocites were calculated for all samples, as a basic indicator of the resistance of the material under the action of cavitation. The change in the morphology of the surface with the test time was followed by scanning electron microscopy. Based on the values of cavitation velocity and analysis of the surface damage morphology, the cavitation resistance of the tested samples based on pyrophillite was determined. The obtained results indicate that the samples of sintered pyrophillite have satisfactory resistance to the action of cavitation and be applied in conditions of lower cavitation loads.", publisher = "Inženjersko društvo za koroziju", journal = "Zaštita materijala", title = "Određivanje otpornosti na dejstvo kavitacije uzoraka pirofilita, Determination of resistance to cavitation of pyrophyllite samples", pages = "134-126", number = "2", volume = "62", doi = "10.5937/zasmat2102126A" }
Andrić, L., Pavlović, M., Dojčinović, M.,& Radulović, D.. (2021). Određivanje otpornosti na dejstvo kavitacije uzoraka pirofilita. in Zaštita materijala Inženjersko društvo za koroziju., 62(2), 126-134. https://doi.org/10.5937/zasmat2102126A
Andrić L, Pavlović M, Dojčinović M, Radulović D. Određivanje otpornosti na dejstvo kavitacije uzoraka pirofilita. in Zaštita materijala. 2021;62(2):126-134. doi:10.5937/zasmat2102126A .
Andrić, Ljubiša, Pavlović, Marko, Dojčinović, Marina, Radulović, Dragan, "Određivanje otpornosti na dejstvo kavitacije uzoraka pirofilita" in Zaštita materijala, 62, no. 2 (2021):126-134, https://doi.org/10.5937/zasmat2102126A . .