The influence of long-term aging on the properties of TEMPO oxidized cotton

Abstract

Cotton yarns were 2,2,6,6-tetramethy|piperidine-1-oxy radical (TEMPO) oxidized, i.e., oxidation was carried out in the presence of sodium hypochlorite, sodium bromide and TEMPO, during different time intervals (30, 60 and 120 min). Given that TEMPO oxidized cotton is prone to aging processes, the influence of long-term aging on the properties of TEMPO oxidized cotton yarns was monitored through changes in their content of carboxyl and aldehyde groups, crystallinity index and water retention value, determined immediately after TEMPO oxidations and 10 years later. The content of carboxyl and aldehyde groups was determined by the calcium acetate method, the crystallinity index by the Schwertassek method, and the water retention value by the standard centrifuge method (ASTM D 2402-78, 1978). Aged TEMPO oxidized cotton yarns showed increased content of carboxyl groups, decreased content of aldehyde groups, unchanged crystallinity index and increased water retention value.

Pamučne pređe su oksidisane 2,2,6,6-tetrametilpiperidin-I-oksilradikal (TEMPO), tj. oksidisane su sa natrijum-hipohloritom, natrijum-bromidomi TEMPO, tokom različitih vremenskih intervala (30, 60 i 120 min). S obzirom na to da je TEMPO oksidisani pamuk podložan procesima starenja, uticaj dugotrajnog starenja na svojstava TEMPO oksidisanih pamučnih pređa praćen je kroz promene u njihovom sadržaju karboksilnih i aldehidnih grupa, indeksu kristalnosti i sposobnosti zadržavanja vode, određenim neposredno nakon TEMPO oksidacije i 10 godina kasnije. Sadržaj karboksilnih i aldehidnih grupa određen je kalcijum-acetatom metodom, indeks kristalnosti Schwertassek-ovom metodom, a sposobnost zadržavanja vode standardnom metodom centrifugiranja (ASTM D 2402-78, 1978). Ostarele TEMPO oksidisane pamučne pređe pokazale su povećan sadržaj karboksilnih grupa, smanjen sadržaj aldehidnih grupa, nepromenjen indeks kristalnosti i povećanu sposobnost zadržavanja vode.