Specific Properties of Polyester Fabrics Functionalized by RF Plasma and Colloidal TiO2 Nanoparticles
(Department of Materials, Textiles and Chemical Engineering, 2009)
This study was aimed to examine the possibility of using RF plasma at low pressure for the surface activation of polyester fabrics in order to improve the binding efficiency of colloidal TiO2 nanoparticles. Colloidal TiO2 ...
Structure sensitivity of dimethylamine deep oxidation over Pt/Al2O3 catalysts
(Elsevier, 2009)
The deep oxidation of dimethylamine (DMA) was studied over Pt/Al2O3 catalysts with small (1 nm) and large (7.8-15.5 nm) Pt crystallite sizes. The turnover frequency (TOF) was higher for the large than for the small Pt ...
Stability of Metal-Oxide Varistor Characteristics in Exploitation Conditions
(Acta Physica Polonica A, 2009)
Wide-spread use of metal-oxide varistors for non-linearity over-voltage protection results in a variety of possible working conditions. It is therefore essential to have a thorough insight into their reliability in various ...
Effect of different fermentation parameters on bioethanol production from corn meal hydrolyzates by free and immobilized cells of Saccharomyces cerevisiae var. ellipsoideus
(Wiley, Hoboken, 2009)
BACKGROUND: Bioethanol produced from renewable biomass, such as corn meal, is a biofuel that is both renewable and environmentally friendly. Significant scientific and technological investments will be needed to achieve ...
Synthesis and characterization of MoOx-Pt/C and TiOx-Pt/C nano-catalysts for oxygen reduction
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The oxygen reduction reaction (ORR) was studied at carbon supported MoOx-Pt/C and TiOx-Pt nanocatalysts in 0.5 mol dm(-3) HClO4 solution, at 25 degrees C. The MoOx-Pt/C and TiOx-Pt/C catalysts were prepared by the polyole ...
Nanosilica/PMMA composites obtained by the modification of silica nanoparticles in a supercritical carbon dioxide-ethanol mixture
(Springer, New York, 2009)
Nanosilica/poly(methyl methacrylate) (PMMA) composites are used to improve the mechanical properties of neat PMMA polymer. In order to obtain superior mechanical properties, it is essential to achieve good bonding between ...
Preparation and characterization TiOx-Pt/C catalyst for hydrogen oxidation reaction
(Royal Soc Chemistry, Cambridge, 2009)
The hydrogen oxidation reaction (HOR) was studied at the home made TiOx-Pt/C nanocatalysts in 0.5 mol dm(-3) HClO4 at 25 degrees C. Pt/C catalyst was first synthesized by modified ethylene glycol method (EG) on commercially ...
The antibacterial efficiency of polyester fabrics modified by air RF plasma and silver nanoparticles
(University of Gent : Department of Materials, Textiles and Chemical Engineering, 2009)
The aim of this study was to highlight the possibility of using the air RF plasma for fiber surface activation that can facilitate the deposition of silver nanoparticles from colloid onto the polyester fabrics and thus, ...
Comparative study of cu(2+) adsorption on a zeolite, a clay and a diatomite from Serbia
(Applied Clay Science, 2009)
The adsorption of a zeolite, clay and diatomite from Serbia toward aqueous Cu2+ ions was studied, at different pH. The adsorbents were characterized with respect to phase composition, specific surface area and point of ...
Micromechanical estimates of the critical values of j-integral for the steel of steam pipelines
(Springer, New York, 2009)
We analyze the level of damage to 14MoV63 steel for steam pipelines under the conditions of crack-growth initiation according to the mechanism of ductile fracture. The state of the material after service for about 100,000 ...