Electrospun Alumina Fibers Doped With Ferric and Magnesium Oxides
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
It is well known that alumina possesses good mechanical and chemical properties. Nanofibers having alpha - alumina structure was used as reinforcement for metal, polymer and ceramic matrix composites. In this study, three ...
Structure and Microstructure Characterization of the La2SrB10O19 Glass-ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The crystal structure of new lanthanum strontium borate glass-ceramics was refined by the Rietveld method. The results showed that La2SrB10O19 has the monoclinic crystal structure, space group C2 (No. 5) with a = 11.1170(6), ...
Structure and photocatalytic properties of sintered TiO2 nanotube arrays
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
One-dimensional (1D) TiO2 nanotubes perpendicular to the substrate were obtained by electrochemical oxidation of titanium foil in an acid electrolyte. In order to alter the crystallinity and the morphology of films the ...
Final Flotation Waste Kinetics of Sintering at Different Heating Regimes
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
In the copper extraction, especially during the process of flotation enrichment and the pyrometallurgical processing, the waste materials that represent huge polluters of environment are being generated. In order to examine ...
Microstructural Characterization and Adsorption Properties of Alkali-Activated Materials Based on Metakaolin
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The microstructural characterization and adsorption properties of metakaolin (MK) and alkali-activated metakaolin, known as geopolymer materials (GP) were investigated. The structure and properties of the metakaolin and ...
Photocatalytic Degradation of Bisphenol A with alpha-Fe2O3 Fibers and Particles
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Two-step synthesis of Fe2O3 particles, performed by precipitation from iron(III) chloride (FeCl3 center dot 6H(2)O) using ammonium hydroxide in first step and calcination at 400 and 700 degrees C during 4 h, provided Fe2O3 ...
Impact of Alumina Particles on the Morphology and Mechanics of Hybrid Wood Plastic Composite Materials
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Hybrid composite panels of Wood-Plastic Composites (WPC) consisting of wood and poly (methyl methacrylate) (PMMA) were reinforced with alumina particles and made by "hot pressing" method. Alumina-based particles were made ...
Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation ...
Influence of the damage level during quenching on thermal shock behavior of low cement castable
(International Institute for the Science of Sintering, Beograd, 2010)
In the recent decades, the use of unshaped monolithic refractories has been increasing greatly because of their significant advantages over other shaped refractory bricks of the same class. A low cement high alumina castable ...
Improvement of the mechanical properties of spark plasma sintered hap bioceramics by decreasing the grain size and by adding multi-walled carbon nanotubes
(International Institute for the Science of Sintering, Beograd, 2013)
Composites based on HAP and oxidized multi-walled carbon nanotubes (o-MWCNT) and monophase HAP materials were processed by spark plasma sintering. Starting from stoichiometric nano-sized HAP powder, monophase bioceramics ...