Thermal shock behavior of alumina based refractories
(Techna Srl, Faenza, 2002)
Temperature difference and fracture resistance parameters have been used to predict the thermal shock behavior. Alumina based commercial refractories with different content of Al2O3 from 28% to 78% were used. Thermal and ...
Influence of drying constant and diffusivity on clay drying behavior
(Techna Srl, Faenza, 2007)
The influence of the correlation between the drying constant and the diffusion coefficient of the liquid on the behavior of two raw materials for brick manufacturing during their drying process was examined. The test was ...
Synthesis of nanostructured boehmite powder by sol-gel method from industrial Na-aluminate solution
(Techna Srl, Faenza, 2003)
Supersaturated Na-aluminate solution from KAP's Alumina plant Bayer process was chosen, as a precursor to synthesize low sodium content nanostructured boehmite powder. Firstly, the solution, was neutralized with strong ...
Hermal shock behavior of Alumina based refractories: Korrelation between damage resistance parameters and water fcuench test
(Techna Srl, Faenza, 2000)
Klaterials were five alumina based commercial refractories with different content of (AI2O3 +TiO2) from 28% to 78%.The thermal and mechanBl properties of these materials were measured using standard laboratory procedure.Thermal ...
Thermal shock behavior of alumina based refractories: correlation between damage resistance parameters and water quench test
(Techna Srl, Faenza, 2000)
Materials were five alumina based commercial refractories with different content of (Al2O3 + TiO2) from 28% to 78%.The thermal and mechanical properties of these materials were measured using standard laboratory procedure. ...