Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
In this work the hydrogen evolution reaction (HER) at Ni-Sn alloy coatings, deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) SnCl2 + 0.3 mol dm(-3) NiCl2 in the pyrophosphate-glycine ...
Incorporation of Pt, Ru and Pt-Ru nanoparticles into ordered mesoporous carbons for efficient oxygen reduction reaction in alkaline media
(Electrochimica Acta, 2015)
Ordered mesoporous carbon, volume-doped up to 3w.% with Pt, Ru and Pt-Ru nanoparticles was synthesized by evaporation-induced self-assembly method, under acidic conditions. The content of incorporated metal was determined ...
Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction
(Electrochimica Acta, 2006)
The kinetics of hydrogen oxidation reaction was studied in perchloric acid solution on carbon-supported Pt nanoparticles using the rotating disk electrode technique. Carbon cryogel and commercial carbon black. Vulcan XC-72 ...
Kinetics of the hydrogen evolution reaction on Fe-Mo film deposited on mild steel support in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2005)
The mechanism and kinetics of the hydrogen evolution reaction were studied. in 1.0 mol dm(-3) NaOH solution on Fe-Mo alloy electrodes prepared by electrodeposition at constant current densities from a pyrophosphate bath. ...
The effect of the electrode surface roughness at low level of coarseness on the polarization characteristics of electrochemical processes
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
In this study, it is considered: (a) the effect of the exchange current density to the limiting diffusion current density ratio (J(0)/J(L)) at low level of surface coarseness on the polarization characteristics of the ...
Ti substrate coated with composite Cr–MoO2 coatings as highly selective cathode materials in hypochlorite production
(Elsevier, 2013)
The aim of this work was to investigate the possibility of preparation of the composite Cr–MoO2 coatings onto steel and titanium substrates as cathode materials with high selective properties which imply the suppression ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Elsevier, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm−3 NaOH, at 25 °C. Tungsten-carbide islands on nano-tungsten particles (WC) was ...
The origin of high activity of Pt-Au surfaces in the formic acid oxidation
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
We have investigated the oxidation of HCOOH on Au-modified Pt (Au"Pt) and Pt-modified Au (Pt")/Au) electrodes to establish the role of the ensemble and the electronic effect in the catalysis of this reaction. The surfaces ...
Methanol electrooxidation on supported Pt and PtRu catalysts in acid and alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2002)
The kinetics of methanol oxidation on supported 47.5 wt.% Pt and 54 wt.% Pt-Ru (with nominal Pt:Ru ratios of 2:3) catalysts are measured in 0.5 M H2SO4 and 0.1 NaOH at 295 and 333 K using thin-film rotating disk electrode ...
Catalysis of oxygen reduction on Au modified by Pd nanoislands in perchloric acid solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
Oxygen reduction reaction (ORR) was studied on polycrystalline gold, Au(poly), modified by nanosized palladium islands in 0.1 M HClO4 solution using rotating disc electrode technique. Paladium was spontaneously deposited ...