Electrochemical and sorption characteristics of metacryloxypropyltrimethoxysilane coatings / Elektrohemijske i sorpcione karakteristike prevlaka metakriloksipropiltrimetoksisilana
(Engineering Society for Corrosion, Belgrade, Serbia, 2008)
The aim of this work was to investigate the influence of deposition parameters (silane solution concentration, deposition time, curing time) on electrochemical and sorption characteristics of metacryloxypropyltrimethoxysilane ...
The influence of hot-dip galvanized steel surface pretreatment on the adhesion of epoxy coating / Uticaj pripreme površine pocinkovanog čelika na adheziju epoksidne prevlake
(Engineering Society for Corrosion, Belgrade, Serbia, 2007)
The influence of hot-dip galvanized steel surface pretreatment on the adhesion of epoxy cataphoretic coating was investigated. Several passive films were formed on hot-dip galvanized steel (phosphate, chromate and oxide). ...
Characterization of electrochemically synthesized pani on graphite electrode for potential use in electrochemical power sources / Elektrohemijska sinteza i karakterizacija elektrode od polianilina za potencijalnu upotrebu u elektrohemijskim izvorima energije
(Engineering Society for Corrosion, Belgrade, Serbia, 2009)
Polyaniline (PANI) on graphite electrode was synthesized electrochemically under galvanostatic condition at current density of 2.0 mA cm-2 from aqueous solution of 1.0 moldm-3 HCl and 0.25 mol dm-3 aniline monomer. ...
Electrochemical synthesis and corrosion behavior of thin polyaniline film on mild steel / Elektrohemijska sinteza i koroziono ponašanje tankih filmova polianilina na mekom čeliku
(Engineering Society for Corrosion, Belgrade, Serbia, 2003)
The electrochemical synthesis of polyaniline (PANI) on mild steel from the sodium-benzoate solutions has been investigated. It has been concluded that thin, highly adherent, polyaniline films could be obtained by anodic ...
Characterization of electrochemically synthesized pani on graphite electrode for potential use in electrochemical power sources / Elektrohemijska sinteza i karakterizacija elektrode od polianilina za potencijalnu upotrebu u elektrohemijskim izvorima energije
(Inženjersko društvo za koroziju, Beograd, 2009)
Polyaniline (PANI) on graphite electrode was synthesized electrochemically under galvanostatic condition at current density of 2.0 mA cm-2 from aqueous solution of 1.0 moldm-3 HCl and 0.25 mol dm-3 aniline monomer. ...
The influence of electrochemically deposited zinc alloys on steel on the protective properties of cathaporetic epoxy coatings / Uticaj elektrohemijski taloženih legura cinka na čeliku na zaštitna svojstva epoksidne kataforetske prevlake
(Engineering Society for Corrosion, Belgrade, Serbia, 2005)
Prior to cathaporetic epoxy coating deposition steel surface was modified by chemical deposition of hot dip galvanized steel and by electrochemical deposition of zinc alloys with iron group of elements (Ni, Co and Fe). The ...
Korozija metala - šta je to?
(Engineering Society for Corrosion, Belgrade, Serbia, 2004)
Korozija materijala je opšte poznat i prihvaćen izraz, ali da li se baš tačno zna šta je korozija? Pod pojmom korozija materijala se podrazumeva svako neželjeno razaranje materijala kao posledice delovanja spoljne sredine. ...
Valorization of gallium from acidic zinc's liquor / Valorizacija galijuma iz kiselog cinkovog luga
(Engineering Society for Corrosion, Belgrade, Serbia, 2007)
In this paper are showed the results of valorisation of gallium, that is gallium salt gallium(III) chloride, GaCl3, by adsorption with chelate resin and then by extraction with 1, 5 mol/dm3 HCI to GaCl3. The efficiency of ...
Formation of approximate differential equations for electrical and molar conductivity determinations of sulfuric acid aqueous solution / Formiranje aproksimacionih diferencijalnih jednačina za određivanje električne i molarne provodljivosti vodenog rastvora sumporne kiseline
(Engineering Society for Corrosion, Belgrade, Serbia, 2005)
In this paper formation of linear differential equations for approximate determination of electrical and molar conductivity of sulfuric-acid solutions, has been give.
Corrosion protection of aluminum by vinyltriethoxysilane coatings / Koroziona stabilnost prevlaka viniltrietoksisilana
(Engineering Society for Corrosion, Belgrade, Serbia, 2008)
In this work the influence of the deposition parameters, i.e. silane solution concentration, deposition time and curing time on the corrosion stability of vinyltriethoxysilane (VTES) coatings on aluminum was investigated. ...