Crystallization kinetics of K2O·TiO2· 3GeO2 glass studied by DTA
(International Institute for the Science of Sintering, 2008)
Crystallization kinetics of K2O·TiO2· 3GeO2 glass was investigated by differential thermal analysis (DTA). Experiments were performed on powder samples with a particle size < 0.037 mm. The glass samples were heated at ...
Influence of the damage level during quenching on thermal shock behavior of low cement castable
(International Institute for the Science of Sintering, Beograd, 2010)
In the recent decades, the use of unshaped monolithic refractories has been increasing greatly because of their significant advantages over other shaped refractory bricks of the same class. A low cement high alumina castable ...
The effect of Y2O3 addition on thermal shock behavior of magnesium aluminate spinel
(International Institute for the Science of Sintering, Beograd, 2009)
The effect of yttria additive on the thermal shock behavior of magnesium aluminate spinel has been investigated. As a starting material we used spinel (MgAl2O4) obtained by the modified glycine nitrate procedure (MGNP). ...
Improvement of the mechanical properties of spark plasma sintered hap bioceramics by decreasing the grain size and by adding multi-walled carbon nanotubes
(International Institute for the Science of Sintering, Beograd, 2013)
Composites based on HAP and oxidized multi-walled carbon nanotubes (o-MWCNT) and monophase HAP materials were processed by spark plasma sintering. Starting from stoichiometric nano-sized HAP powder, monophase bioceramics ...
The use of image analysis for determination of surface deterioration level of improved alumina based materials subjected to cavitation
(International Institute for the Science of Sintering, Beograd, 2013)
Alumina based specimens having different content of alumina based fibers were investigated for possible application as cavitation resistant material. Cavitation damages of the alumina based specimens were tested by the ...
Characterization of MgAl2O4 Sintered Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in ...
Structure and Microstructure Characterization of the La2SrB10O19 Glass-ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The crystal structure of new lanthanum strontium borate glass-ceramics was refined by the Rietveld method. The results showed that La2SrB10O19 has the monoclinic crystal structure, space group C2 (No. 5) with a = 11.1170(6), ...
Sintered materials based on copper and alumina powders synthesized by a novel method
(International Institute for the Science of Sintering, Beograd, 2010)
This paper presents the production of sintered materials from nano-composite powders obtained by a novel synthesis method, which represents a combination of thermochemical synthesis and mechanical alloying. Produced powders ...
Evolution of Structural and Functional Properties of the Fe/BaTiO3 System Guided by Mechanochemical and Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2020)
Multiferroic systems are attractive to the researches worldwide due to diversity of existing applications, as well as possible novel ones. In order to contribute to understanding of the processes that take place within the ...
Anisotropy Analysis of Low Cement Concrete by Ultrasonic Measurements and Image Analysis
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The analized material was high alumina low cement castable sintered at three different temperatures. Influence of initial material anisotropy on the thermal shock resistance as well as changes of anisotropy level during ...