Radical polymerization of monoethyl itaconate / Radikalna polimerizacija monoetil itakonata
(Association of Chemical Engineers of Serbia, 2003)
The radical polymerization of monoethyl itaconate (MEI) was investigated in bulk and in solution at 60°C using a,a'-azobisisobutyronitrile as initiator. It was established that the obtained polymer poly(monoethyl itaconate) ...
Factors influencing the removal of divalent cations by hydroxyapatite
(Elsevier, Amsterdam, 2008)
The effect of pH, contact time, initial metal concentration and presence of common competing cations, on hydroxyapatite (HAP) sorption properties towards Ph2+, Cd2+, Zn2+, and Sr2+ ions was studied and compared using a ...
Kinetics of the zinc anodic dissolution reaction in near neutral EDTA solutions / Kinetika anodnog rastvaranja cinka u blisko neutralnim rastvorima EDTA
(Serbian Chemical Society, Belgrade, 2003)
Polarization curves of the anodic dissolution reaction of zinc were determined in EDTA solutions of different total molar concentrations (0.05 0.10, 0.15 and 0.20 mol dm-3), the pH values of which were systematically varied ...
Nonlinear FR-ZLC method for investigation of adsorption equilibrium and kinetics
(Springer, New York, 2008)
A new method for investigation of adsorption equilibrium and kinetics, named Nonlinear Frequency Response-Zero Length Column (NFR-ZLC) method, is introduced. It combines the advantages of the Nonlinear FR method (the ...
The thermal degradation of poly(diethyl fumarate)
(Elsevier Sci Ltd, Oxford, 2006)
The kinetics and mechanism of the thermal degradation of poly(diethyl fumarate) (PDEF) were studied by thermogravimetry, as well as by analysis of the thermolysis volatiles and polymer residue. The characteristic mass loss ...
The kinetics of the thermal degradation of isomeric dipropyl and dibutyl esters of poly(itaconic acid)
(Pergamon-Elsevier Science Ltd, Oxford, 2000)
Non-oxidative and oxidative thermogravimetry was performed on poly(di-n-propyl-) (PDnPI), poly(di-iso-propyl-) (PDiPI), poly(di-n-butyl-) (PDnBI), poly(di-iso-butyl-) (PDiBI) and poly(di-sec-butyl itaconate) (PDsBI). The ...
The thermal degradation of poly(diethyl fumarate) / Termička degradacija poli(dietil fumarata)
(Association of Chemical Engineers of Serbia, 2001)
The kinetics and mechanism of the thermal degradation of poly(diethyl tumarate) (PDEF) were studied by thermogravimetry and analysis of the polymer residue. The characteristic mass loss temperatures were determined, as ...
Non-isothermal crystallization of k2o center dot tio2 center dot 3geo(2) glass
(Springer, Dordrecht, 2009)
The crystallization of K2O center dot TiO2 center dot 3GeO(2) glass under non-isothermal condition was studied. In powdered glass with particle sizes less than 0.15 mm, surface crystallization was dominant and an activation ...
Experimental design approach regarding kinetics of high pressure leaching processes / Dizajniranje eksperimenata u pogledu na kinetiku luženja pri visokim pritiscima
(Savez inženjera metalurgije Srbije, Beograd, 2003)
Kinetics of high pressure leaching of nickel latente ore "Rudjinci", Serbia was studied in this work. The following parameters: temperature, acid to ore ratio, stirring speed, and time were optimized in order to obtain the ...
The thermal stability of poly(sec-butyl methacrylate) / Termička stabilnost poli(sec-butil metakrilata)
(Društvo inženjera plastičara i gumara, Beograd, 2000)
The thermal stability of a series of poly(sec-butyl methacrylate)(PsBMA) samples was investigated by non-isothermal thermogravimetry (TG). The PsBMA samples were synthesised by bulk radical polymerization in the presence ...