Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
The effect of heat treatment on toughness and wear resistance of Fe-Cr-C-Nb alloys / Uticaj termičke obrade na žilavost i otpornost na habanje Fe-Cr-C-Nb legura
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Alloying with niobium improves the mechanical properties of the high chromium irons. The alloy containing appriximately 3 %Nb gives the best compromise between wear resistance and toughness. These properties were improved ...
Cavitation damages morphology of high-strength low-alloy steel
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper presents the research into behaviour of HSLA steel affected by cavitation. The parent material (PM) and simulated heat-affected zone (SHAZ) were studied. Ultrasonic vibratory cavitation test was performed in ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Development of contemporary procedures for lead obtaining / Razvoj savremenih postupaka dobijanja olova
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Contemporary procedures of lead concentrates treatment were in different expansion during last thirty years. All procedures have in common the following: smelting reaction proceeds in solid-gas suspension, melting products ...
Dynamic recrystallization in M2 tool steel during friction welding
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Friction welding of M2 tool steel and 1730 quenched and tempered steel was performed with the aim to reveal the origin of extremely fine martensitic grain in M2 steel after welding. Taking into account thermomechanical ...
Microstructure evolution of the hot-rolled modified AA 5083 alloys during the two stage thermal treatment
(Savez inženjera metalurgije Srbije, Beograd, 2011)
The effects of the two stage heat treatment on the structure of two hot-rolled 5083 aluminum alloys without and with 0.12% Zr addition were investigated. Combination of the metallographic and transmission electron microscopy ...
A two-stage metal valorisation process from electric arc furnace dust (eafd)
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper demonstrates possibility of separate zinc and lead recovery from coal composite pellets, composed of EAFD with other synergetic iron-bearing wastes and by-products (mill scale, pyrite-cinder, magnetite concentrate), ...
The influence of thermomechanical treatment on recrystallization of AlMg4.5Cu0.5 alloy
(Savez inženjera metalurgije Srbije, Beograd, 2007)
Recrystallization behavior of an Al-Mg-Cu alloy (4.5 wt. %Mg and 0.45 wt %Cu) subjected to different thermomechanical treatments (TMTs) have been studied by means of light optical microscopy and hardness measurements. In ...
The recycling of high magnesium aluminum alloys estimation of the most reliable procedure
(Savez inženjera metalurgije Srbije, Beograd, 2009)
Aluminum is one of the most recyclable materials. Namely, the properties of aluminum are not affected by the recycling and reuse, thus enable that high value of the metal is maintained after reprocessing. The re-smelting ...