Structure and kinetics of internal oxidation in Ag-Sn alloys

Abstract

Internal oxidation in Ag-Sn-In-Te and Ag-Sn-Cu-Bi alloys was tested. micro structures of casted and homogenized samples, as well as after internal oxidation were followed by optical microscopy. The structure of Ag-Sn-Cu-Bi alloy was found finer, and the oxidation rate is considerably higher compared to the Ag-Sn-In-Te type alloy sheets. It seems that the size and volume fraction of secondary phase particles (probably ζ type) can influence the process of internal oxidation. In the Ag-Sn-In-Te alloy type 'wavy oxidation' was noticed with oxide free regions. .

U radu su prikazani rezultati ispitivanja mogućnosti primene interne oksidacije kod legura Ag-Sn-In-Te i Ag-Sn-Cu-Bi dobijenih putem ingot metalurgije. Ispitivanja su obuhvatila karakterizaciju mikrostrukture legura u livenom stanju, nakon homogenizacije na 8000C i posle interne oksidacije na 7000C u slobodnoj atmosferi vazduha. Dobijeni rezultati ukazuju na mogućnost da proces oksidacije usporavaju u strukturi prisutne čestice sekundarne faze (najverovatnije intermetalne ζ-faze). U oksidisanom sloju Ag-Sn-In-Te legura zapaža se pojava talasaste interne oksidacije. Kod obe legure tipa Ag-Sn-In-Te je zapažena pojava i eksterne oksidacije koja brzo dovodi do pasivizacije. Ispitivanja kinetike oksidacije pokazala su da je brzina oksidacije kod Ag-Sn-In-Te legura u odnosu na Ag-Sn-Cu-Bi niža. .