Electrochemical polymerization of Polyaniline (PANI) film on aluminum electrode from aqueous solution of 0.20 mol dm-3 sodium benzoate containing 0.25 mol dm-3 aniline have been investigated using potentiodinamic and galvanostatic techniques. Corrosion behavior of aluminum and PANI coated aluminum electrode during initial exposure to 3% NaCl have been investigated using electrochemical potentiodimanic and impedance spectroscopy technique (EIS). It was observed that thin PANI coating of estimated thickness of 10μm had provided good initial corrosion protection of aluminum in3% NaCl, decreasing the corrosion current density at least 15 times.
TY - CONF
AU - Gvozdenović, Milica
AU - Jugović, Branimir
AU - Grgur, Branimir
PY - 2010
UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/1573
AB - Electrochemical polymerization of Polyaniline (PANI) film on aluminum electrode from aqueous solution of 0.20 mol dm-3 sodium benzoate containing 0.25 mol dm-3 aniline have been investigated using potentiodinamic and galvanostatic techniques. Corrosion behavior of aluminum and PANI coated aluminum electrode during initial exposure to 3% NaCl have been investigated using electrochemical potentiodimanic and impedance spectroscopy technique (EIS). It was observed that thin PANI coating of estimated thickness of 10μm had provided good initial corrosion protection of aluminum in3% NaCl, decreasing the corrosion current density at least 15 times.
PB - Nice : International Society of Electrochemistry
C3 - The 61st Annual Meeting of the International Society of Electrochemistry: Electrochemistry from Biol
T1 - Electrochemical synthesis and corrosion properties of polyaniline coating on aluminum
SP - 06-P-034
ER -
@conference{
author = "Gvozdenović, Milica and Jugović, Branimir and Grgur, Branimir",
year = "2010",
url = "http://TechnoRep.tmf.bg.ac.rs/handle/123456789/1573",
abstract = "Electrochemical polymerization of Polyaniline (PANI) film on aluminum electrode from aqueous solution of 0.20 mol dm-3 sodium benzoate containing 0.25 mol dm-3 aniline have been investigated using potentiodinamic and galvanostatic techniques. Corrosion behavior of aluminum and PANI coated aluminum electrode during initial exposure to 3% NaCl have been investigated using electrochemical potentiodimanic and impedance spectroscopy technique (EIS). It was observed that thin PANI coating of estimated thickness of 10μm had provided good initial corrosion protection of aluminum in3% NaCl, decreasing the corrosion current density at least 15 times.",
publisher = "Nice : International Society of Electrochemistry",
journal = "The 61st Annual Meeting of the International Society of Electrochemistry: Electrochemistry from Biol",
title = "Electrochemical synthesis and corrosion properties of polyaniline coating on aluminum",
pages = "06-P-034"
}
Gvozdenović, M., Jugović, B.,& Grgur, B. (2010). Electrochemical synthesis and corrosion properties of polyaniline coating on aluminum.
The 61st Annual Meeting of the International Society of Electrochemistry: Electrochemistry from Biol
Nice : International Society of Electrochemistry., 06-P-034.
Gvozdenović M, Jugović B, Grgur B. Electrochemical synthesis and corrosion properties of polyaniline coating on aluminum. The 61st Annual Meeting of the International Society of Electrochemistry: Electrochemistry from Biol. 2010;:06-P-034
Gvozdenović Milica, Jugović Branimir, Grgur Branimir, "Electrochemical synthesis and corrosion properties of polyaniline coating on aluminum" The 61st Annual Meeting of the International Society of Electrochemistry: Electrochemistry from Biol (2010):06-P-034