Incorporation of Pt, Ru and Pt-Ru nanoparticles into ordered mesoporous carbons for efficient oxygen reduction reaction in alkaline media
(Electrochimica Acta, 2015)
Ordered mesoporous carbon, volume-doped up to 3w.% with Pt, Ru and Pt-Ru nanoparticles was synthesized by evaporation-induced self-assembly method, under acidic conditions. The content of incorporated metal was determined ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Polarization curves in the ohmic controlled electrodeposition of metals
(Oxford : Pergamon-Elsevier Science Ltd, 2009)
The conditions under which ohmic controlled metal electrodeposition occurs are discussed using a simple mathematical model. it is shown that ohmic controlled electrodeposition can be operative if the value of the exchange ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Elsevier, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm−3 NaOH, at 25 °C. Tungsten-carbide islands on nano-tungsten particles (WC) was ...