New types of protective coatings and development of test methods / Nove vrste zaštitnih premaza i razvoj metoda ispitivanja
(Society for Structural Integrity and Life (DIVK), 2023)
The paper presents the results of synthesis and characterisation of refractory coatings based on various fillers
intended for the protection of metallic structures. Refractory
fillers applied are based on mullite, ...
Cavitation resistance of composite polyester resin/basalt powder
(Society for Structural Integrity and Life, Institute for Material Testing, 2019)
The paper presents the results of research on cavitation resistance of the composite based on unsaturated polyester resin and basalt powder, as reinforcement. Basalt powder was obtained by grinding and micronising basaltic ...
Integrity assessment of reverse engineered ti-6al-4v eli total hip replacement implant
(Society for Structural Integrity and Life, Institute for Material Testing, 2019)
Total hip replacement implants are used as an artificial replacement for disfunctional hips in order to sustain joint movement. Chosen material and design of total hip replacement are the most influential factors for ...
Cavitation resistance of turbine runner blades at the hydropower plant 'Djerdap'
(Society for Structural Integrity and Life, Institute for Material Testing, 2017)
Hydropower plants need to develop means of protection of turbine and hydromechanical equipment from undesirable occurrences, such as degradation of parent material and/or weld metal of parts and structures caused by stresses ...
Behaviour of nionikral-70 in low-cycle fatigue
(Society for Structural Integrity and Life, Institute for Material Testing, 2017)
Experimental research on the behaviour of high-strength low-alloy steel ( HSLA)exposed to low-cycle fatigue (LCF) with controlled and fully reversible strain (Delta epsilon/2 = const, R epsilon =epsilon(min)/epsilon(max) ...
Analysis of fracture behaviour of thin s316l stainless steel plates
(Institut za ispitivanje materijala, Beograd, 2017)
In this paper are presented experimental analyses of the behaviour of 316L stainless steel in regard to fracture, according to standard methods of investigation on modified tensile C(T) specimens. The S316L alloy is selected ...
Effect of plasma hardfacing and carbides presence on the occurrence of cracks and microcracks
(Society for Structural Integrity and Life, Institute for Material Testing, 2018)
Presented is the effect of plasma hardfacing (or just hardfacing) and carbides presence on the occurrence of cracks and microcracks in the welded layer. The reasons behind this phenomenon are analysed and explained. In ...
TRANSIENT TEMPERATURE FIELDS EFFECTS ON MULTI-PASS WELDING IN A BUTT JOINT OF AUSTENITIC PIPING / UTICAJI PRELAZNIH TEMPERATURSKIH POLJA NA VIŠEPROLAZNO ZAVARIVANJE U SUČEONOM SPOJU AUSTENITNIH CEVI
(Society for Structural Integrity and Life (DIVK), 2023)
This work uses computational thermomechanical model-based finite element analysis (FEA) to explore the effects of welding sequences on residual stresses that accumulate in the material and distortions of welded components, ...
Integrity assessment of vital beam components that enable conjoint operation of two bridge cranes
(Society for Structural Integrity and Life, Institute for Material Testing, 2018)
Vital components of the beam that enable conjoint operation of two bridge cranes are braces and threaded spindle. The beam connects two bridge cranes with overall lifting capacity of 500 t (2 x 250 t) and enables their ...
Influence of defects on limit loads and integrity of the pipeline at hydropower plant 'Pirot'
(Society for Structural Integrity and Life, Institute for Material Testing, 2020)
Topic of this work is the integrity assessment of the pipeline section from hydropower plant Pirot. Crack-like defect size, maximum depth, is determined based on non-destructive evaluation - the largest crack depth is taken ...