Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Structural characteristics of some ternary Ag-In-Sn alloys
(Savez inženjera metalurgije Srbije, Beograd, 2008)
The Ag-In-Sn system, as one of potential lead-free solder materials, was studied in this paper. The investigated alloys were chosen from two sections, with molar ratio of In:Sn equal to 1:4; 1:2. DTA, XRD, SEM and micro ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
The influence of the cellular structure of the seed on the structure single crystal superalloy based on Ni / Uticaj ćelijske strukture klice na strukturu monokristala superlegure na bazi Ni
(Savez inženjera metalurgije Srbije, Beograd, 2003)
This paper elaborates the investigations about influence of the cellular structure of the seed to the distance between primary dendrites, λ1 Investigations were performed on superalloy single crystals based Ni which were ...
On the Al-Mg alloy sheets for automotive application: Problems and solutions
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Aluminium alloys suitable for automotive application were reviewed briefly as well as the reasons for the future wider application of Al-Mg type alloys. Basic problems related to the limited consumption of Al-Mg type alloy ...
Hydrometallurgical process for extraction of metals from electronic waste, part II: Development of the processes for the recovery of copper from printed circuit boards (PCB)
(Savez inženjera metalurgije Srbije, Beograd, 2011)
Rapid technological development induces increase of generation of used electric and electronic equipment waste, causing a serious threat to the environment. Waste printed circuit boards (WPCBs), as the main component of ...
The influence of the interface shape on the plane-to-cellular-to-dendritic transition in superalloy based of nickel
(Savez inženjera metalurgije Srbije, Beograd, 2004)
In this paper investigation of the influence of the crystallization conditions on the interface shape during the solidification of Ni-based Superalloy by Vertical Bridgman method were investigated. The samples were undertaken ...