The influence of the aging time of RuO2 and TiO2 sols on the electrochemical properties and behavior for the chlorine evolution reaction of activated titanium anodes obtained by the sol-gel procedure
(Elsevier, 2000)
The influence of the aging time of RuO2 and TiO2 sols used for the preparation of (40% RuO2+60% TiO2)/Ti anodes by the sol-gel procedure on the electrochemical properties and behavior for the chlorine evolution reaction ...
Methanol oxidation on an ink type electrode using Pt supported on high area carbons
(Pergamon-Elsevier Science Ltd, Oxford, 2001)
Methanol oxidation was investigated on the following Pt catalysts: bare Pt electrode, Pt covered by nafion (R) film, and pt catalysts supported on high area carbons in the form of an ink. The reaction was carried out using ...
Synthesis and characterization of MoOx-Pt/C and TiOx-Pt/C nano-catalysts for oxygen reduction
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The oxygen reduction reaction (ORR) was studied at carbon supported MoOx-Pt/C and TiOx-Pt nanocatalysts in 0.5 mol dm(-3) HClO4 solution, at 25 degrees C. The MoOx-Pt/C and TiOx-Pt/C catalysts were prepared by the polyole ...
Kinetic analysis of hydrogen evolution at Ni-Mo alloy electrodes
(Elsevier Science Ltd, 2000)
The hydrogen evolution reaction (HER) on Ni, Mo and MoNi intermetallic compound was investigated with ac impedance and dc polarization measurements in 1.0 mol dm-3 NaOH solution at 25 °C. The rate constants of the forward ...
Kinetics of the hydrogen evolution reaction on Fe-Mo film deposited on mild steel support in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2005)
The mechanism and kinetics of the hydrogen evolution reaction were studied. in 1.0 mol dm(-3) NaOH solution on Fe-Mo alloy electrodes prepared by electrodeposition at constant current densities from a pyrophosphate bath. ...
Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction
(Electrochimica Acta, 2006)
The kinetics of hydrogen oxidation reaction was studied in perchloric acid solution on carbon-supported Pt nanoparticles using the rotating disk electrode technique. Carbon cryogel and commercial carbon black. Vulcan XC-72 ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Polarization curves in the ohmic controlled electrodeposition of metals
(Oxford : Pergamon-Elsevier Science Ltd, 2009)
The conditions under which ohmic controlled metal electrodeposition occurs are discussed using a simple mathematical model. it is shown that ohmic controlled electrodeposition can be operative if the value of the exchange ...
The origin of high activity of Pt-Au surfaces in the formic acid oxidation
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
We have investigated the oxidation of HCOOH on Au-modified Pt (Au"Pt) and Pt-modified Au (Pt")/Au) electrodes to establish the role of the ensemble and the electronic effect in the catalysis of this reaction. The surfaces ...
Methanol electrooxidation on supported Pt and PtRu catalysts in acid and alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2002)
The kinetics of methanol oxidation on supported 47.5 wt.% Pt and 54 wt.% Pt-Ru (with nominal Pt:Ru ratios of 2:3) catalysts are measured in 0.5 M H2SO4 and 0.1 NaOH at 295 and 333 K using thin-film rotating disk electrode ...