Wear resistance and dynamic fracture toughness of hypoeutectic high-chromium white cast iron alloyed with niobium and vanadium
(Institute of Metals and Technology, 2014)
The influence of mass fractions 1.5 % Nb and 1.5 % V, added singly and in combination, on the microstructural characteristics and properties relevant to the service performance of the hypoeutectic high-chromium white iron ...
Influence of the thermo-mechanical treatment on the exfoliation and pitting corrosion of an aa5083-type alloy
(Institute of Metals and Technology, 2014)
Exfoliation and pitting corrosion were tested on an AA5083-type alloy sheet, after applying different thermo-mechanical treatments. Hot-rolled plates were laboratory cold rolled with 16-54 % reductions, and subsequently ...
Synthesis of α-Al2O3 based foams with improved properties as catalyst carriers
(Institute of Metals and Technology, 2014)
This paper explores the possibility of synthesising catalyst supports with improved properties. Alumina foams were produced with the polymer replication technique. Representative high- and low-temperature sintering ceramics ...
Optimization of the recycling processes for magnesium from a highly contaminated waste
(Institute of Metals and Technology, 2014)
With the recently increased use of magnesium alloys, especially in the automotive industry, a large quantity of generated waste, based on magnesium alloys, is expected. Such a waste often contains many impurities such as ...
Geopolymerization of low-grade bauxite
(Institute of Metals and Technology, 2014)
In terms of quality, bauxite ore can be classified as high- or low-grade ore. High-grade bauxite ores are used for alumina extraction using the Bayer process, while low-grade bauxite ores have a limited application. In ...