Relationship between the calculated oxygen activity and the sulfur partition ratio for cao-al2o3-sio2-mgo slag during ladle refining
(Institute of Metals and Technology, 2012)
A slag-metal equilibrium study was carried out to investigate the effect of oxygen activity on the sulfur partition for CaO-Al2O3-SiO2-MgO slag. The sulfide capacity C-s prediction models by Sosinsky-Sommerville based on ...
Reduction of ultra-fine tungsten powder with tungsten (vi) oxide in a vertical tube reactor
(Institute of Metals and Technology, 2011)
The reduction of WO(3) with hydrogen in a vertical tube reactor is a new approach to the reduction of tungsten oxide compared to conventional procedures in a stationary layer. The advantage of this method is the intensive ...
Influence of the matrix type on the temperature responsiveness of a poly-nipaam/chitosan microgel functionalized pes fabric
(Institute of Metals and Technology, 2013)
In this paper, the temperature responsiveness (swelling/de-swelling) of the poly-NiPAAm/chitosan (PNCS) microgel applied to a PBS fabric in combination with two different matrixes, i.e., 1,2,3,4-butanetetracarboxylic acid ...
Influence of the thermo-mechanical treatment on the exfoliation and pitting corrosion of an aa5083-type alloy
(Institute of Metals and Technology, 2014)
Exfoliation and pitting corrosion were tested on an AA5083-type alloy sheet, after applying different thermo-mechanical treatments. Hot-rolled plates were laboratory cold rolled with 16-54 % reductions, and subsequently ...
Wear resistance and dynamic fracture toughness of hypoeutectic high-chromium white cast iron alloyed with niobium and vanadium
(Institute of Metals and Technology, 2014)
The influence of mass fractions 1.5 % Nb and 1.5 % V, added singly and in combination, on the microstructural characteristics and properties relevant to the service performance of the hypoeutectic high-chromium white iron ...
The nano-wetting aspect at the liquid-metal/sic interface
(Inst Za Kovinske Materiale I In Tehnologie, Ljubjana, 2015)
The wetting process on the nano-scale, as an initial and essential step in liquid metal/ceramic joining, is discussed here. Thanks to recent breakthroughs in experimental techniques with nanometre resolution, questions ...
Homogenization of an al-mg alloy and alligatoring failure: alloy ductility and fracture
(Inst Za Kovinske Materiale I In Tehnologie, Ljubjana, 2016)
High-strength Al-Mg alloys have a propensity toward hot fracture and failure by alligatoring during hot rolling. In this study the effect of homogenization conditions on the susceptibility of an Al-5.1Mg-0.7Mn alloy toward ...
Synthesis of α-Al2O3 based foams with improved properties as catalyst carriers
(Institute of Metals and Technology, 2014)
This paper explores the possibility of synthesising catalyst supports with improved properties. Alumina foams were produced with the polymer replication technique. Representative high- and low-temperature sintering ceramics ...
Multi-criteria analysis of synthesis methods for ni-based catalysts
(Inst Za Kovinske Materiale I In Tehnologie, Ljubjana, 2016)
Catalysts based on the Ni/Al2O3 system are used in a variety of catalytic processes. Catalysts are commonly synthesized through thermochemical routes (impregnation, precipitation, coprecipitation and others). The authors ...
Aspects of titanium-implant surface modification at the micro and nano levels
(Institute of Metals and Technology, 2012)
The shape and chemical composition, as well as the macro- and microtopography, of an implant surface have been studied widely as the major factors that positively influence implant osseointegration. Titanium and titanium ...