Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation ...
Influence of the damage level during quenching on thermal shock behavior of low cement castable
(International Institute for the Science of Sintering, Beograd, 2010)
In the recent decades, the use of unshaped monolithic refractories has been increasing greatly because of their significant advantages over other shaped refractory bricks of the same class. A low cement high alumina castable ...
Improvement of the mechanical properties of spark plasma sintered hap bioceramics by decreasing the grain size and by adding multi-walled carbon nanotubes
(International Institute for the Science of Sintering, Beograd, 2013)
Composites based on HAP and oxidized multi-walled carbon nanotubes (o-MWCNT) and monophase HAP materials were processed by spark plasma sintering. Starting from stoichiometric nano-sized HAP powder, monophase bioceramics ...
Mechanical properties of biomorphic silicon carbide ceramics
(International Institute for the Science of Sintering, Beograd, 2011)
Biomorphous β-SiC ceramics were produced from linden wood by impregnation with tetraethyl orthosilicate (TEOS), followed pyrolysis and high temperature treatment at 1580°C. Six specimen groups included charcoal and five ...
SiC synthesis using natural Mg-silicates
(International Institute for the Science of Sintering, Beograd, 2012)
The silicon carbide powders are prepared by carbothermal reduction of domestic mineral resources (white and brown sepiolite), at relatively low temperatures (1200 - 1600oC). Carbothermal reduction process is greatly ...
Influence of sintering temperature on raw and beneficiated clay 'Klokoti'
(International Institute for the Science of Sintering, Beograd, 2012)
The raw clay 'Klokoti' from middle Bosnia was beneficiated by method of wet separation which results in removing fraction over 20 μm. The raw clay was characterized by chemical composition, grain size distribution and ...
Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the ...
Mechanical properties correlation to processing parameters for advanced alumina based refractories
(International Institute for the Science of Sintering, Beograd, 2012)
Alumina based refractories are usually used in metallurgical furnaces and their thermal shock resistance is of great importance. In order to improve thermal shock resistance and mechanical properties of alumina based ...
The use of image analysis for determination of surface deterioration level of improved alumina based materials subjected to cavitation
(International Institute for the Science of Sintering, Beograd, 2013)
Alumina based specimens having different content of alumina based fibers were investigated for possible application as cavitation resistant material. Cavitation damages of the alumina based specimens were tested by the ...
Characterization of MgAl2O4 Sintered Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in ...