The possibility of obtaining. Composite al18wt%si/sic by compocasting process
Само за регистроване кориснике
2012
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The aim of this study was to investigate the influence of various process parameters on the microstructure of composite materials based on alloys All 8Wt%Si with the addition of 10Wt%SiC. The effect of stirring speed (1000 and 1500 rpm), stirring time 15 min and casting temperature 565 degrees C on the structural and mechanical properties are discussed. It was found that applying the stirring speed of 1500 rpm in semisolid state the best distribution of SiC particles in the matrix was achieved, which gave satisfying mechanical properties. In order to evaluate the quality of obtained composites and their possible application in the practice, tests were carried out under conditions of cavitation. Cavitation damage to the composite samples was determined using modified vibratory cavitation equipment. Mass loss and surface analysis of composite samples during the experiment were used as an indicator the level of cavitation damage. The results showed very good cavitation resistance which gi...ves the possibility of using these materials in condition where cavitation resistance is needed.
Кључне речи:
Al-Si alloys / composite / composasting process / cavitation resistanceИзвор:
Modtech 2012: New Face of T M C R, Vols I and II, 2012, 249-252Издавач:
- Modtech Publishing House, Iasi
Финансирање / пројекти:
- Serbian Ministry of Science and Education, Republic of Serbia
- Развој технолошких поступака ливења под утицајем електромагнетног поља и технологија пластичне прераде у топлом стању четворокомпонентних легура Al-Zn за специјалне намене (RS-MESTD-Technological Development (TD or TR)-34002)
- Усмерена синтеза, структура и својства мултифункционалних материјала (RS-MESTD-Basic Research (BR or ON)-172057)
- Развој и примена мултифункционалних материјала на бази домаћих сировина модернизацијом традиционалних технологија (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45008)
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Ćosić, Milena AU - Acimović-Pavlović, Zagorka AU - Terzić, Anja AU - Dojčinović, Marina AU - Pavlović, Ljubica PY - 2012 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/2164 AB - The aim of this study was to investigate the influence of various process parameters on the microstructure of composite materials based on alloys All 8Wt%Si with the addition of 10Wt%SiC. The effect of stirring speed (1000 and 1500 rpm), stirring time 15 min and casting temperature 565 degrees C on the structural and mechanical properties are discussed. It was found that applying the stirring speed of 1500 rpm in semisolid state the best distribution of SiC particles in the matrix was achieved, which gave satisfying mechanical properties. In order to evaluate the quality of obtained composites and their possible application in the practice, tests were carried out under conditions of cavitation. Cavitation damage to the composite samples was determined using modified vibratory cavitation equipment. Mass loss and surface analysis of composite samples during the experiment were used as an indicator the level of cavitation damage. The results showed very good cavitation resistance which gives the possibility of using these materials in condition where cavitation resistance is needed. PB - Modtech Publishing House, Iasi T2 - Modtech 2012: New Face of T M C R, Vols I and II T1 - The possibility of obtaining. Composite al18wt%si/sic by compocasting process EP - 252 SP - 249 UR - https://hdl.handle.net/21.15107/rcub_technorep_2164 ER -
@article{ author = "Ćosić, Milena and Acimović-Pavlović, Zagorka and Terzić, Anja and Dojčinović, Marina and Pavlović, Ljubica", year = "2012", abstract = "The aim of this study was to investigate the influence of various process parameters on the microstructure of composite materials based on alloys All 8Wt%Si with the addition of 10Wt%SiC. The effect of stirring speed (1000 and 1500 rpm), stirring time 15 min and casting temperature 565 degrees C on the structural and mechanical properties are discussed. It was found that applying the stirring speed of 1500 rpm in semisolid state the best distribution of SiC particles in the matrix was achieved, which gave satisfying mechanical properties. In order to evaluate the quality of obtained composites and their possible application in the practice, tests were carried out under conditions of cavitation. Cavitation damage to the composite samples was determined using modified vibratory cavitation equipment. Mass loss and surface analysis of composite samples during the experiment were used as an indicator the level of cavitation damage. The results showed very good cavitation resistance which gives the possibility of using these materials in condition where cavitation resistance is needed.", publisher = "Modtech Publishing House, Iasi", journal = "Modtech 2012: New Face of T M C R, Vols I and II", title = "The possibility of obtaining. Composite al18wt%si/sic by compocasting process", pages = "252-249", url = "https://hdl.handle.net/21.15107/rcub_technorep_2164" }
Ćosić, M., Acimović-Pavlović, Z., Terzić, A., Dojčinović, M.,& Pavlović, L.. (2012). The possibility of obtaining. Composite al18wt%si/sic by compocasting process. in Modtech 2012: New Face of T M C R, Vols I and II Modtech Publishing House, Iasi., 249-252. https://hdl.handle.net/21.15107/rcub_technorep_2164
Ćosić M, Acimović-Pavlović Z, Terzić A, Dojčinović M, Pavlović L. The possibility of obtaining. Composite al18wt%si/sic by compocasting process. in Modtech 2012: New Face of T M C R, Vols I and II. 2012;:249-252. https://hdl.handle.net/21.15107/rcub_technorep_2164 .
Ćosić, Milena, Acimović-Pavlović, Zagorka, Terzić, Anja, Dojčinović, Marina, Pavlović, Ljubica, "The possibility of obtaining. Composite al18wt%si/sic by compocasting process" in Modtech 2012: New Face of T M C R, Vols I and II (2012):249-252, https://hdl.handle.net/21.15107/rcub_technorep_2164 .