Dynamic mechanical properties of aramid fabrics impregnated with multiwalled carbon nanotubes

Abstract

Carbon nanotubes (CNT) represent allotropes of carbon with a cylindrical nanostructure. In multiwalled carbon nanotubes (MWCNT), graphitic layers make up concentric tubes. The multiwalled nanotubes length in our research is from 3 µm to 30 µm and their outer diameter is from 13 nm to 18 nm. Their purity is greater than 99 wt.%. The carbon nanotubes possess extraordinary physical properties, great electrical and thermal conductivity. The addition of carbon nanotubes as the reinforcement in polymer composites can significantly improve the composite mechanical properties. In the study, the pristine multiwalled carbon nanotubes (MWCNT) were introduced in order to additionally enhance mechanical properties of materials for ballistic protection.

Ugljenične nanocevi (carbon nanotubes, CNT) predstavljaju alotropsku modifikaciju ugljenika cilindrične nanostrukture. Kod višeslojnih ugljeničnih nanocevi (multiwalled carbon nanotubes, MWCNT), grafitni slojevi obrazuju koncentrične cevi. U našem istraživanju dužina višeslojnih nanocevi iznosi od 3 µm do 30 µm i njihov spoljašnji prečnik je od 13 nm do 18 nm. Njihova čistoća je veća od 99 mas.%. Ugljenične nanocevi imaju izvanredna fizička svojstva, veliku električnu i toplotnu provodljivost. Njihovim dodatkom u vidu ojačanja u polimernim kompozitima se mogu značajno poboljšati mehanička svojstva kompozita. U ovom radu su čiste višeslojne ugljenične nanocevi bile korišćene sa ciljem da se poboljšaju mehanička svojstva materijala za zaštitu u balistici.