Dynamic mechanical properties of aramid fabrics impregnated with carbon nanotube/poly (vinyl butyral)/ethanol solution

Abstract

In this study six samples of polyurethane/p-aramid multiaxial fabric forms (Colon fabrics) were coated with 10 wt.% poly (vinyl butyral) (PVB)/ethanol solution with the addition of multiwalled carbon nanotubes (MWCNT). The solution was impregnated on both sides of each of the fabrics. All composite samples consisted of four layers of the impregnated fabrics. The MWCNT/PVB content was 0, 0.1 and 1 wt.%. The three samples of the fabrics with different MWCNT/PVB content were coated with y-aminopropyltriethoxysilane (AMEO silane)/ethanol solution due to the surface modification. The mechanical properties of the prepared composite samples were studied by dynamic mechanical analysis (DMA). The 60% increase in storage modulus was achieved by addition of MWCNT and impregnation of aramid fabrics with AMEO silane. The pristine multiwalled carbon nanotubes (MWCNT) were introduced in order to enhance additionally the mechanical properties of the materials for ballistic protection.