Failures of brass condenser tubes
Нема приказа
Аутори
Bobić, BiljanaJegdić, Bore
Jugović, Branimir
Stevanović, Jasmina
Gligorijević, Bojan
Murariu, Alin
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Causes of failure of brass condenser tubes (CuZn28Sn1) in a thermal power plant in Serbia are analysed. Results of testing by Fourier transformed infrared spectroscopy (FTIR) have indicated the presence of ammonia and nitrogen compounds on fracture surfaces and on the inner surface of the tubes. These compounds are specific agents that cause stress corrosion cracking (SCC) in brass. Analysis of fracture surfaces using scanning electron microscopy (SEM) has shown the brittle transgranular fracture due to the occurrence of SCC. The resistance of brass condenser tubes to other types of corrosion, such as erosion, general and selective corrosion (dezincification) is also considered. Some procedures are proposed to reduce the risk of SCC in the brass condenser tubes.
Кључне речи:
condenser tubes / brass / stress corrosion cracking / dezincificationИзвор:
Structural Integrity and Life, 2016, 16, 1, 19-23Издавач:
- Society for Structural Integrity and Life, Institute for Material Testing
Финансирање / пројекти:
- Истраживање и оптимизација технолошких и функционалних перформанси вентилационог млина термоелектране Костолац Б (RS-MESTD-Technological Development (TD or TR)-34028)
- Развој триболошких микро/нано двокомпонентних и хибридних самоподмазујућих композита (RS-MESTD-Technological Development (TD or TR)-35021)
Институција/група
Inovacioni centarTY - JOUR AU - Bobić, Biljana AU - Jegdić, Bore AU - Jugović, Branimir AU - Stevanović, Jasmina AU - Gligorijević, Bojan AU - Murariu, Alin PY - 2016 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/3171 AB - Causes of failure of brass condenser tubes (CuZn28Sn1) in a thermal power plant in Serbia are analysed. Results of testing by Fourier transformed infrared spectroscopy (FTIR) have indicated the presence of ammonia and nitrogen compounds on fracture surfaces and on the inner surface of the tubes. These compounds are specific agents that cause stress corrosion cracking (SCC) in brass. Analysis of fracture surfaces using scanning electron microscopy (SEM) has shown the brittle transgranular fracture due to the occurrence of SCC. The resistance of brass condenser tubes to other types of corrosion, such as erosion, general and selective corrosion (dezincification) is also considered. Some procedures are proposed to reduce the risk of SCC in the brass condenser tubes. PB - Society for Structural Integrity and Life, Institute for Material Testing T2 - Structural Integrity and Life T1 - Failures of brass condenser tubes EP - 23 IS - 1 SP - 19 VL - 16 UR - https://hdl.handle.net/21.15107/rcub_technorep_3171 ER -
@article{ author = "Bobić, Biljana and Jegdić, Bore and Jugović, Branimir and Stevanović, Jasmina and Gligorijević, Bojan and Murariu, Alin", year = "2016", abstract = "Causes of failure of brass condenser tubes (CuZn28Sn1) in a thermal power plant in Serbia are analysed. Results of testing by Fourier transformed infrared spectroscopy (FTIR) have indicated the presence of ammonia and nitrogen compounds on fracture surfaces and on the inner surface of the tubes. These compounds are specific agents that cause stress corrosion cracking (SCC) in brass. Analysis of fracture surfaces using scanning electron microscopy (SEM) has shown the brittle transgranular fracture due to the occurrence of SCC. The resistance of brass condenser tubes to other types of corrosion, such as erosion, general and selective corrosion (dezincification) is also considered. Some procedures are proposed to reduce the risk of SCC in the brass condenser tubes.", publisher = "Society for Structural Integrity and Life, Institute for Material Testing", journal = "Structural Integrity and Life", title = "Failures of brass condenser tubes", pages = "23-19", number = "1", volume = "16", url = "https://hdl.handle.net/21.15107/rcub_technorep_3171" }
Bobić, B., Jegdić, B., Jugović, B., Stevanović, J., Gligorijević, B.,& Murariu, A.. (2016). Failures of brass condenser tubes. in Structural Integrity and Life Society for Structural Integrity and Life, Institute for Material Testing., 16(1), 19-23. https://hdl.handle.net/21.15107/rcub_technorep_3171
Bobić B, Jegdić B, Jugović B, Stevanović J, Gligorijević B, Murariu A. Failures of brass condenser tubes. in Structural Integrity and Life. 2016;16(1):19-23. https://hdl.handle.net/21.15107/rcub_technorep_3171 .
Bobić, Biljana, Jegdić, Bore, Jugović, Branimir, Stevanović, Jasmina, Gligorijević, Bojan, Murariu, Alin, "Failures of brass condenser tubes" in Structural Integrity and Life, 16, no. 1 (2016):19-23, https://hdl.handle.net/21.15107/rcub_technorep_3171 .