Analysis of acceleratingly aged composite explosives based upon pentrite and polyurethane binder

Abstract

Composite explosives based upon pentrite and polyurethane binder were artificially aged at 60°C and 80°C. During aging the polymer component degraded faster than pentrite. Aging effects on the samples of composite explosives were examined using DSC. Aging effects on the binder extracted from composite explosives were monitored using infrared spectro-photometry. The decomposition reactions were aproximately of there zero order. IR analysis of the binder has shown that there are some changes in the shape and size of peaks, the tearing of some peaks... .

Istraživanje obuhvata kompozitne eksplozive na bazi pentrita i poliuretanskog veziva koji su ubrzano stareni na temperaturama od 60 i 80ºC. Pri starenju polimerna komponenta brže degradira u odnosu na pentrit. Promene nastale starenjem su ispitane metodom DSC. Pomoću IR su praćene promene nastale na vezivu ekstrahovanom iz uzoraka. Analiza uzoraka DSC je pokazala da su uzorci termijski stabilni. Reakcija dekompozicije je približno prvog reda. IR analizom veziva iz uzoraka uočene su promene oblika i veličine pojedinih pikova, cepanje pikova, promene odnosa u veličini dva susedna pika itd. Promene ne ukazuju na odvijanje značajnih hemijskih procesa, tj. promene u strukturi.