dc.description.abstractThe densification behavior of hydroxyapatite nanorods prepared by chemical precipitation method in open reactor conditions was investigated by application of different heating rates. The non-isothermal processing was performed with 2, 10, and 50 degrees C/min up to 1200 degrees C and yielded fully dense ceramics. The implementation of the higher heating rate provided grain size refinement from micrometer level for the slowest ramp, down to 250 nm in the case of processing with 50 degrees C/min, without any drawbacks regarding final density. The relative amount of retained structural hydroxyl groups in sintered ceramics was gradually increased with the heating rate. Furthermore, the qualitative level of optical translucency was increased with a higher heating rate which can be explained by the beneficial alignment of HAp nanorods during the fast heating rate processing, achieved microstructural refinement, and higher amount of structural hydroxyl groups.en
dc.publisherElsevier Science Bv, Amsterdam
dc.relationinfo:eu-repo/grantAgreement/MESTD/Integrated and Interdisciplinary Research (IIR or III)/45004/RS//
dc.rightsopenAccess
dc.sourceMaterials Letters
dc.titleA facile route for hydroxyapatite densification with an increased heating rateen
dc.typearticle
dc.rights.licenseARR
dc.citation.epage15
dc.citation.other207: 12-15
dc.citation.rankM22
dc.citation.spage12
dc.citation.volume207
dc.identifier.doi10.1016/j.matlet.2017.07.020
dc.identifier.fulltexthttp://TechnoRep.tmf.bg.ac.rs/bitstream/id/1440/3587.pdf
dc.identifier.scopus2-s2.0-85022338548
dc.identifier.wos000407691000004
dc.type.versionpublishedVersion


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу