dc.description.abstractTemperature difference and fracture resistance parameters have been used to predict the thermal shock behavior. Alumina based commercial refractories with different content of Al2O3 from 28% to 78% were used. Thermal and mechanical properties were measured. Thermal shock stability of the samples was measured using water the quench test. Values of temperature difference were calculated using heat transfer conditions and material properties. Calculated values of temperature difference and fracture resistance parameters were compared to results of quench experiments. Linear regression analysis was used to determine the correlation between calaculated values for the critical temperature difference and the damage resistance parameter with the results of water quench test. Excellent correlation with the experimental results was observed for all used equations for prediction of thermal shock behavior of the samples. Correlation between damage resistance parameters, temperature difference and results from the water quench test also are presented.en
dc.publisherTechna Srl, Faenza
dc.rightsrestrictedAccess
dc.sourceIndustrial Ceramics
dc.titleThermal shock behavior of alumina based refractoriesen
dc.typearticle
dc.rights.licenseARR
dc.citation.epage31
dc.citation.issue1
dc.citation.other22(1): 27-31
dc.citation.rankM23
dc.citation.spage27
dc.citation.volume22
dc.identifier.pmid
dc.identifier.rcubconv_7102
dc.identifier.scopus2-s2.0-0036299582
dc.identifier.wos000176067000005
dc.type.versionpublishedVersion


Files in this item

FilesSizeFormatView

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record