Tailored Adhesion Properties of Acrylate Adhesives on Al Alloys by the Addition of Mn-Al-LDH
Autori
Tomić, NatašaSaleh, Mohamed Nasr
Vuksanović, Marija M.
Egelja, Adela
Obradović, Vera
Marinković, Aleksandar
Jančić-Heinemann, Radmila
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
The goal of this study was to investigate the effect of the structure of Mn-Al layered double hydroxide (LDH) on the adhesion behavior of composite adhesives on two Al alloys (L3005 and L8079). The composite adhesives were made out of the UV-curing Bisphenol A glycidylmethacrylate/triethylene glycol dimethacrylate (BT) as polymer matrix and the addition of 1, 3, and 5 wt. % of Mn-Al LDH as adhesion enhancers. Adhesion was evaluated by using the micro Vickers hardness testing procedure. The wetting angle of composite adhesives to the Al substrates was measured and compared to the adhesion parameter b obtained from the microhardness tests. The highest increase in adhesion was observed for BT with 5 wt. % of Mn-Al LDH on L3005 substrate, which was more than 15 times higher than the adhesion for the neat BT. The morphological segregation of composite adhesives after the contact with Al substrates was examined by optical microscopy and a higher compatibility of Mn-Al LDH particles with L300...5 substrate was found. The methods used for the adhesion properties assessment suggested that the Mn-Al LDH was the best adhesion enhancer of the BT matrix for L3005 substrate containing a higher content of Mn and surface hydroxyl groups.
Ključne reči:
layer double hydroxide / composite adhesive / adhesion / interface / aluminumIzvor:
Polymers, 2021, 13, 9Finansiranje / projekti:
- Ministarstvo nauke, tehnološkog razvoja i inovacija Republike Srbije, institucionalno finansiranje - 200135 (Univerzitet u Beogradu, Tehnološko-metalurški fakultet) (RS-MESTD-inst-2020-200135)
- Ministarstvo nauke, tehnološkog razvoja i inovacija Republike Srbije, institucionalno finansiranje - 200287 (Inovacioni centar Tehnološko-metalurškog fakulteta u Beogradu doo) (RS-MESTD-inst-2020-200287)
DOI: 10.3390/polym13091525
ISSN: 2073-4360
PubMed: 34068553
WoS: 000650714500001
Scopus: 2-s2.0-85106589894
Kolekcije
Institucija/grupa
Inovacioni centarTY - JOUR AU - Tomić, Nataša AU - Saleh, Mohamed Nasr AU - Vuksanović, Marija M. AU - Egelja, Adela AU - Obradović, Vera AU - Marinković, Aleksandar AU - Jančić-Heinemann, Radmila PY - 2021 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/4931 AB - The goal of this study was to investigate the effect of the structure of Mn-Al layered double hydroxide (LDH) on the adhesion behavior of composite adhesives on two Al alloys (L3005 and L8079). The composite adhesives were made out of the UV-curing Bisphenol A glycidylmethacrylate/triethylene glycol dimethacrylate (BT) as polymer matrix and the addition of 1, 3, and 5 wt. % of Mn-Al LDH as adhesion enhancers. Adhesion was evaluated by using the micro Vickers hardness testing procedure. The wetting angle of composite adhesives to the Al substrates was measured and compared to the adhesion parameter b obtained from the microhardness tests. The highest increase in adhesion was observed for BT with 5 wt. % of Mn-Al LDH on L3005 substrate, which was more than 15 times higher than the adhesion for the neat BT. The morphological segregation of composite adhesives after the contact with Al substrates was examined by optical microscopy and a higher compatibility of Mn-Al LDH particles with L3005 substrate was found. The methods used for the adhesion properties assessment suggested that the Mn-Al LDH was the best adhesion enhancer of the BT matrix for L3005 substrate containing a higher content of Mn and surface hydroxyl groups. T2 - Polymers T1 - Tailored Adhesion Properties of Acrylate Adhesives on Al Alloys by the Addition of Mn-Al-LDH IS - 9 VL - 13 DO - 10.3390/polym13091525 ER -
@article{ author = "Tomić, Nataša and Saleh, Mohamed Nasr and Vuksanović, Marija M. and Egelja, Adela and Obradović, Vera and Marinković, Aleksandar and Jančić-Heinemann, Radmila", year = "2021", abstract = "The goal of this study was to investigate the effect of the structure of Mn-Al layered double hydroxide (LDH) on the adhesion behavior of composite adhesives on two Al alloys (L3005 and L8079). The composite adhesives were made out of the UV-curing Bisphenol A glycidylmethacrylate/triethylene glycol dimethacrylate (BT) as polymer matrix and the addition of 1, 3, and 5 wt. % of Mn-Al LDH as adhesion enhancers. Adhesion was evaluated by using the micro Vickers hardness testing procedure. The wetting angle of composite adhesives to the Al substrates was measured and compared to the adhesion parameter b obtained from the microhardness tests. The highest increase in adhesion was observed for BT with 5 wt. % of Mn-Al LDH on L3005 substrate, which was more than 15 times higher than the adhesion for the neat BT. The morphological segregation of composite adhesives after the contact with Al substrates was examined by optical microscopy and a higher compatibility of Mn-Al LDH particles with L3005 substrate was found. The methods used for the adhesion properties assessment suggested that the Mn-Al LDH was the best adhesion enhancer of the BT matrix for L3005 substrate containing a higher content of Mn and surface hydroxyl groups.", journal = "Polymers", title = "Tailored Adhesion Properties of Acrylate Adhesives on Al Alloys by the Addition of Mn-Al-LDH", number = "9", volume = "13", doi = "10.3390/polym13091525" }
Tomić, N., Saleh, M. N., Vuksanović, M. M., Egelja, A., Obradović, V., Marinković, A.,& Jančić-Heinemann, R.. (2021). Tailored Adhesion Properties of Acrylate Adhesives on Al Alloys by the Addition of Mn-Al-LDH. in Polymers, 13(9). https://doi.org/10.3390/polym13091525
Tomić N, Saleh MN, Vuksanović MM, Egelja A, Obradović V, Marinković A, Jančić-Heinemann R. Tailored Adhesion Properties of Acrylate Adhesives on Al Alloys by the Addition of Mn-Al-LDH. in Polymers. 2021;13(9). doi:10.3390/polym13091525 .
Tomić, Nataša, Saleh, Mohamed Nasr, Vuksanović, Marija M., Egelja, Adela, Obradović, Vera, Marinković, Aleksandar, Jančić-Heinemann, Radmila, "Tailored Adhesion Properties of Acrylate Adhesives on Al Alloys by the Addition of Mn-Al-LDH" in Polymers, 13, no. 9 (2021), https://doi.org/10.3390/polym13091525 . .