Mechanical properties of biomorphic silicon carbide ceramics
(International Institute for the Science of Sintering, Beograd, 2011)
Biomorphous β-SiC ceramics were produced from linden wood by impregnation with tetraethyl orthosilicate (TEOS), followed pyrolysis and high temperature treatment at 1580°C. Six specimen groups included charcoal and five ...
Influence of the damage level during quenching on thermal shock behavior of low cement castable
(International Institute for the Science of Sintering, Beograd, 2010)
In the recent decades, the use of unshaped monolithic refractories has been increasing greatly because of their significant advantages over other shaped refractory bricks of the same class. A low cement high alumina castable ...
Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation ...
Improvement of the mechanical properties of spark plasma sintered hap bioceramics by decreasing the grain size and by adding multi-walled carbon nanotubes
(International Institute for the Science of Sintering, Beograd, 2013)
Composites based on HAP and oxidized multi-walled carbon nanotubes (o-MWCNT) and monophase HAP materials were processed by spark plasma sintering. Starting from stoichiometric nano-sized HAP powder, monophase bioceramics ...
Mechanical properties correlation to processing parameters for advanced alumina based refractories
(International Institute for the Science of Sintering, Beograd, 2012)
Alumina based refractories are usually used in metallurgical furnaces and their thermal shock resistance is of great importance. In order to improve thermal shock resistance and mechanical properties of alumina based ...
SiC synthesis using natural Mg-silicates
(International Institute for the Science of Sintering, Beograd, 2012)
The silicon carbide powders are prepared by carbothermal reduction of domestic mineral resources (white and brown sepiolite), at relatively low temperatures (1200 - 1600oC). Carbothermal reduction process is greatly ...
Structural, Chemical and Magnetic Properties of Nickel Vertical Posts Obtained by Glancing Angle Deposition Technique
(Science of Sintering, 2017)
In this work, Glancing Angle Deposition technique was used for obtaining nanostructured nickel thin film with vertical posts on glass substrate which was positioned 75 degrees with respect to the substrate normal and rotated ...
Influence of sintering temperature on raw and beneficiated clay 'Klokoti'
(International Institute for the Science of Sintering, Beograd, 2012)
The raw clay 'Klokoti' from middle Bosnia was beneficiated by method of wet separation which results in removing fraction over 20 μm. The raw clay was characterized by chemical composition, grain size distribution and ...
Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the ...
Comparison of Morphological Parameters of Ceramic Materials Surface Damage Exposed to Thermal Shock and Cavitation Erosion
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The surface defects on the samples, which are based on alumina, exposed to thermal shocks and cavitations erosion were analyzed using image analysis. For both types of experimental testing, the samples are made of the same ...