Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Cavitation damages morphology of high-strength low-alloy steel
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper presents the research into behaviour of HSLA steel affected by cavitation. The parent material (PM) and simulated heat-affected zone (SHAZ) were studied. Ultrasonic vibratory cavitation test was performed in ...
Hydrometallurgical process for extraction of metals from electronic waste, part II: Development of the processes for the recovery of copper from printed circuit boards (PCB)
(Savez inženjera metalurgije Srbije, Beograd, 2011)
Rapid technological development induces increase of generation of used electric and electronic equipment waste, causing a serious threat to the environment. Waste printed circuit boards (WPCBs), as the main component of ...
Possibility of secondary lead slag stabilization in concrete with presence of selected additives
(Savez inženjera metalurgije Srbije, Beograd, 2010)
A comparative technical and environmental evaluation of products arising from the stabilization/solidification of secondary lead metallurgical slag into a cement matrix was performed. Provided samples of an industrial slag ...
Influence of Cr, Mn and Mo on structure and properties of V microalloyed medium carbon forging steels
(Savez inženjera metalurgije Srbije, Beograd, 2010)
The influence of Cr, Mo and Mn on microstructure and mechanical properties of V-microalloyed medium-carbon steels has been studied by means of metallography and mechanical testing. Cr, Mn and Mo addition promotes the ...
Effect of heating rate on precipitation of peak-aged Al-Li (8091) alloy: A quantitative approach
(Savez inženjera metalurgije Srbije, Beograd, 2010)
Samples of Al-Li (8091) alloy were solution treated at 540ºC for 30 min, water-quenched and continuously heated in oil at 0.05 and 0.1ºC/min rates, from room temperature to 190ºC when the peak hardness was achieved. Having ...
The analysis of the tribological properties of multiple strengthened nanocomposite of the Cu-Al2o3 system
(Savez inženjera metalurgije Srbije, Beograd, 2011)
This paper presents the results of examined tribological properties of the multiple strengthened nanocomposite Cu-Al2O3 system. Cu-Al2O3 composite powder was obtained by combination of the thermo-chemical procedure and ...