Cavitation damage of the medium carbon steel: Implementation of image analysis
(Elsevier Science Bv, Amsterdam, 2008)
Cavitation damage of the medium carbon steel was performed using the modified vibratory cavitation test set up. Erosion rates were measured by analytical method. The morphology of damage under cavitation action was determined ...
Using the image analysis program for prediction of thermal stability behavior of refractory specimen
(8th International Symposium on Multifunctional and Functionally Graded Materials, FGM2004, 2005)
Most important properties which are usually measured for refractories are work temperature and thermal stability. Thermal stability of the alumina based samples was measured using a standard laboratory procedure, the water ...
A fracture mechanics approach to thermal shock investigation in alumina-based refractory
(9th International Conference on Multiscale and Functionally Graded Materials, FGM IX, 2008)
The thermal shock behavior of large grain size, alumina-based refractories was investigated experimentally using a standard water quench test. A mathematical model was employed to simulate the thermal stability behavior. ...
Determination of thermal shock resistance of silicon carbide/cordierite composite material using nondestructive test methods
(Elsevier Sci Ltd, Oxford, 2008)
In the present work Mg-exchanged zeolit and silicon carbide were used as starting materials for obtaining cordierite/SiC composite ceramics with weight ratio 30:70 and 50:50. Behavior of composite ceramics after thermal ...
Rotating disk alumina precursor fiber formation process stability determination using image analysis
(Savez inženjera metalurgije Srbije, Beograd, 2002)
Precursor fibers are made from the aluminium-hydroxide chloride based sols. The process stability can be influenced both by the fiber formation conditions and the rheology of the sol. The distance from the disk canter is ...
An improved method for thermal stability behavior characterization of silicon carbide/cordierite composite material
(Savez inženjera metalurgije Srbije, Beograd, 2007)
In the present work Mg-exchanged zeolit and silicon carbide were used as starting materials for obtaining cordierite/SiC composite ceramics with weight ratio 50:50. Samples were exposed to the water quench test from 950°C, ...
The use of image analysis for the interaction of 1,3,5-trisubstituted isocyanurates with oxidizer and different binders in composite materials / Korišćenje analize slike za utvrđivanje interakcije 1,3,5-trisupstituisanih izocijanurata sa oksidansom i različitim vezivima u kompozitnim gorivima
(Association of Chemical Engineers of Serbia, 2006)
Composite propellants are non-homogenous propellants and comprise primarily crystalline oxidizer and metal fuels uniformly suspended in a resin binder. The strength of the bonds between the polymer matrix and the oxidizer ...
Assessment of viscoelastic crack bridging toughening in refractory materials
(Elsevier Sci Ltd, Oxford, 2008)
Viscoelastic bridges can be formed in refractory ceramics while cooling from high temperatures. Such bridges can shield crack tips, thus reducing the effective crack tip stress intensity factors leading to higher resistance ...
The use of image analysis program for the determination of surface deterioration of refractory specimen during thermal shock / Korišćenje programa za analizu slike za određivanje stepena oštećenja vatrostalnog uzorka pri termošoku
(Društvo za ispitivanje i istraživanje materijala i konstrukcija Srbije, Beograd, 2006)
During examination of refractory specimen, one of the most important characteristics is their resistance to thermal shock. Standard method of testing is based on monitoring the surface shanging during thermal stability ...
Influence of formation conditions and precursor viscosity on mean fiber diameter formed using the relating disk method
(Elsevier, Amsterdam, 2000)
Alumina ceramic fibers were produced from aluminum-hydroxidechloride based sol. Polyvinyl alcohol and surface active material were applied to adjust the rheological characteristics of the: sol. The rotating disk formation ...