Characterization of nano-powder morphology obtained by ultrasonic spray pyrolysis
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Spherical nanosized particles of copper were synthesized by ultrasonic dispersion of solutions from copper sulphate in the temperature range of 800-900°C in hydrogen atmosphere. A controlled particle size was realized ...
Determination of AL2O3particle size in Cu-AL2O3 nanocomposite materials using UV spectrophotometry / Određivanje veličine čestica AL2O3 u nanokompozitnim materijalima iz sistema Cu-AL2O3 primenom UV spektrofotometrije
(Savez inženjera metalurgije Srbije, Beograd, 2008)
In order to achieve improved mechanical properties of dispersion strengthened nanocomposite, without influencing electrical and thermal conductivity it is necessary for dispersoide to be nano sized and uniformly distributed ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
The effect of heat treatment on toughness and wear resistance of Fe-Cr-C-Nb alloys / Uticaj termičke obrade na žilavost i otpornost na habanje Fe-Cr-C-Nb legura
(Savez inženjera metalurgije Srbije, Beograd, 2008)
Alloying with niobium improves the mechanical properties of the high chromium irons. The alloy containing appriximately 3 %Nb gives the best compromise between wear resistance and toughness. These properties were improved ...
Cavitation damages morphology of high-strength low-alloy steel
(Croatian Metallurgical Soc, Zagreb, 2016)
This paper presents the research into behaviour of HSLA steel affected by cavitation. The parent material (PM) and simulated heat-affected zone (SHAZ) were studied. Ultrasonic vibratory cavitation test was performed in ...
On the Al-Mg alloy sheets for automotive application: Problems and solutions
(Savez inženjera metalurgije Srbije, Beograd, 2004)
Aluminium alloys suitable for automotive application were reviewed briefly as well as the reasons for the future wider application of Al-Mg type alloys. Basic problems related to the limited consumption of Al-Mg type alloy ...