Ti substrate coated with composite Cr–MoO2 coatings as highly selective cathode materials in hypochlorite production
(Elsevier, 2013)
The aim of this work was to investigate the possibility of preparation of the composite Cr–MoO2 coatings onto steel and titanium substrates as cathode materials with high selective properties which imply the suppression ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Elsevier, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm−3 NaOH, at 25 °C. Tungsten-carbide islands on nano-tungsten particles (WC) was ...
Polarization curves in the ohmic controlled electrodeposition of metals
(Oxford : Pergamon-Elsevier Science Ltd, 2009)
The conditions under which ohmic controlled metal electrodeposition occurs are discussed using a simple mathematical model. it is shown that ohmic controlled electrodeposition can be operative if the value of the exchange ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
Hydrogen evolution in acid solution at Pd electrodeposited onto Ti2AlC
(Pergamon-Elsevier Science Ltd, Oxford, 2017)
The hydrogen evolution reaction (HER) was studied in 0.5 M H2SO4 at 25 degrees C on Pd electrodeposited onto Ti2AlC substrate, as an excellent substrate due to its high conductivity and high stability in concentrated ...
Methanol oxidation on an ink type electrode using Pt supported on high area carbons
(Pergamon-Elsevier Science Ltd, Oxford, 2001)
Methanol oxidation was investigated on the following Pt catalysts: bare Pt electrode, Pt covered by nafion (R) film, and pt catalysts supported on high area carbons in the form of an ink. The reaction was carried out using ...
The effect of the electrode surface roughness at low level of coarseness on the polarization characteristics of electrochemical processes
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
In this study, it is considered: (a) the effect of the exchange current density to the limiting diffusion current density ratio (J(0)/J(L)) at low level of surface coarseness on the polarization characteristics of the ...
Oxygen reduction on iron-IV. The reduction of hydrogen peroxide as the intermediate in oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1991)
The kinetics of hydrogen peroxide reduction were studied on iron in borate buffered and unbuffered solutions of pH ranging from 8.6 to 13.8, with and without the presence of chloride ions. A rotating disk electrode was ...
Oxygen reduction on iron-Part VI. Processes in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1994)
The kinetics of oxygen reduction were studied on passivated iron in borate buffered and unbuffered solutions of pH ranging from 7.4 to 13.8. A rotating disk electrode was employed. The O2 reduction on iron under these ...
Hydrogen peroxide oxidation on passive iron in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1992)
The kinetics of hydrogen peroxide oxidation were studied on passive iron in alkaline solutions of pH ranging from 9.8 to 13.8, using the rotating disk electrode. Measurements were taken using the linear sweep technique. ...