Thermodynamic and structural investigation of the Ag-In-Sb system
(Croatian Metallurgical Society, 2007)
The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution mode!, are presented ...
Experimental design approach regarding kinetics of high pressure leaching processes / Dizajniranje eksperimenata u pogledu na kinetiku luženja pri visokim pritiscima
(Savez inženjera metalurgije Srbije, Beograd, 2003)
Kinetics of high pressure leaching of nickel latente ore "Rudjinci", Serbia was studied in this work. The following parameters: temperature, acid to ore ratio, stirring speed, and time were optimized in order to obtain the ...
Shot-peening induced twinning in ship-building steel / Dvojnikovanje u brodskom limu kao posledica tretiranja u mlazu sačme
(Savez inženjera metalurgije Srbije, Beograd, 2002)
The aim of this work to simulate a shot-peening process and reveal the final microstructure. The latter consisted of rafinated ferritic grains, with occurrence of twins in some grains. Since the twinning occurs when a very ...
The growth of germanijum single crystal in the universal multizone crystallization furnace by application of the electronic Bridgman-Stocbarger method / Rast monokristala germanijuma u univerzalnom multizonskom kristalizatoru primenom elektronske Bridgman-Stocbarger metode
(Savez inženjera metalurgije Srbije, Beograd, 2002)
This paper examines the possibility of the application of multizone furnace, i.e. universal multizone crystallizator furnace in obtaining germanijum (Ga added) single crystal using electronic Bridgman-Stocbarger method. ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (hsla) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Structural characteristics of some ternary Ag-In-Sn alloys
(Savez inženjera metalurgije Srbije, Beograd, 2008)
The Ag-In-Sn system, as one of potential lead-free solder materials, was studied in this paper. The investigated alloys were chosen from two sections, with molar ratio of In:Sn equal to 1:4; 1:2. DTA, XRD, SEM and micro ...
Identification of low cycle fatigue parameters of high strength low-alloy (hsla) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Suitability of heat treatment for crack resistance of material in the connection part of heavy transporter for liquid slag
(Croatian Metallurgical Soc, Zagreb, 2014)
The post weld heat treatment (PWHT) was used to reduce the level of the residual stresses and increase of the crack resistance of the material in the connection part.The article presents the results of the residual stress ...
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheet
(Savez inženjera metalurgije Srbije, Beograd, 2005)
Deformation behavior of the AlMg4.5Cu0.5 type alloy sheets was examined after cold rolling and annealing in the range of temperature from 220°C to 520°C, water quenching and natural aging. The low temperature annealed ...
Microstructural investigation of the heat-affected zone of simulated welded joint of p91 steel
(Croatian Metallurgical Society, 2013)
In the process of testing teal components exposed to elevated temperature, it is hot possible to neglect Cracks. The most significant cracks can be induced by welding, which is applied for joining of Structural components. ...