Microstructural characteristics of calcium hydroxyapatite/poly-L-lactide based composites
Само за регистроване кориснике
1999
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Besides its high osteoinductive properties, hydroxyapatite (HAp) exhibits a relatively low mechanical strength. In order to improve the mechanical properties and reliability of HAp based composites, the addition of selected polymers is highly recommended, The main objective of this work is to study the microstructural characteristics of HAp/poly-L-lactide (PLLA) composites obtained by cold or hot processing. The composites were prepared from a mixture of a chloroform solution of poly-L-lactide with granulated HAp. After elimination of chloroform by vacuum evaporation, dense compacts were obtained by cold or hot pressing. The pressing pressure ranged from 98.10 to 294.3 MPa for both cold and hot pressing, The hot pressing was performed in the temperature region 293-457 K for a time period of 15-60 min. Depending on the PLLA amount and the pressing procedure it is possible to obtain highly porous or nearly fully dense composites, The scanning electron microscopy examination of fracture a...s well as of free surfaces revealed that the final porosity and wetting are affected to a great extent by the synthesis conditions and amount of polymer added. An increase in temperature to 457 K for a longer period of time results in fully dense compacts, The formation of a nearly continuous polymer network that leads to the hardening of HAp has also been observed. However, it should be pointed out that some layers of HAp may be free of polymer film since PLLA penetrates more deeply into the porous HAp.
Кључне речи:
biomaterials / bone / Ca-hydroxyapatite / composite / interface / microstructure / phases / poly-L-lactide / pressing temperatureИзвор:
Journal of Microscopy, 1999, 196, 2, 243-248Издавач:
- Wiley, Hoboken
DOI: 10.1046/j.1365-2818.1999.00623.x
ISSN: 0022-2720
PubMed:
WoS: 000083537100017
Scopus: 2-s2.0-0032725721
Институција/група
Tehnološko-metalurški fakultetTY - JOUR AU - Ignjatović, NL AU - Plavšić, Milenko B. AU - Miljković, Miroslav AU - Zivković, LM AU - Uskoković, Dragan PY - 1999 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/233 AB - Besides its high osteoinductive properties, hydroxyapatite (HAp) exhibits a relatively low mechanical strength. In order to improve the mechanical properties and reliability of HAp based composites, the addition of selected polymers is highly recommended, The main objective of this work is to study the microstructural characteristics of HAp/poly-L-lactide (PLLA) composites obtained by cold or hot processing. The composites were prepared from a mixture of a chloroform solution of poly-L-lactide with granulated HAp. After elimination of chloroform by vacuum evaporation, dense compacts were obtained by cold or hot pressing. The pressing pressure ranged from 98.10 to 294.3 MPa for both cold and hot pressing, The hot pressing was performed in the temperature region 293-457 K for a time period of 15-60 min. Depending on the PLLA amount and the pressing procedure it is possible to obtain highly porous or nearly fully dense composites, The scanning electron microscopy examination of fracture as well as of free surfaces revealed that the final porosity and wetting are affected to a great extent by the synthesis conditions and amount of polymer added. An increase in temperature to 457 K for a longer period of time results in fully dense compacts, The formation of a nearly continuous polymer network that leads to the hardening of HAp has also been observed. However, it should be pointed out that some layers of HAp may be free of polymer film since PLLA penetrates more deeply into the porous HAp. PB - Wiley, Hoboken T2 - Journal of Microscopy T1 - Microstructural characteristics of calcium hydroxyapatite/poly-L-lactide based composites EP - 248 IS - 2 SP - 243 VL - 196 DO - 10.1046/j.1365-2818.1999.00623.x ER -
@article{ author = "Ignjatović, NL and Plavšić, Milenko B. and Miljković, Miroslav and Zivković, LM and Uskoković, Dragan", year = "1999", abstract = "Besides its high osteoinductive properties, hydroxyapatite (HAp) exhibits a relatively low mechanical strength. In order to improve the mechanical properties and reliability of HAp based composites, the addition of selected polymers is highly recommended, The main objective of this work is to study the microstructural characteristics of HAp/poly-L-lactide (PLLA) composites obtained by cold or hot processing. The composites were prepared from a mixture of a chloroform solution of poly-L-lactide with granulated HAp. After elimination of chloroform by vacuum evaporation, dense compacts were obtained by cold or hot pressing. The pressing pressure ranged from 98.10 to 294.3 MPa for both cold and hot pressing, The hot pressing was performed in the temperature region 293-457 K for a time period of 15-60 min. Depending on the PLLA amount and the pressing procedure it is possible to obtain highly porous or nearly fully dense composites, The scanning electron microscopy examination of fracture as well as of free surfaces revealed that the final porosity and wetting are affected to a great extent by the synthesis conditions and amount of polymer added. An increase in temperature to 457 K for a longer period of time results in fully dense compacts, The formation of a nearly continuous polymer network that leads to the hardening of HAp has also been observed. However, it should be pointed out that some layers of HAp may be free of polymer film since PLLA penetrates more deeply into the porous HAp.", publisher = "Wiley, Hoboken", journal = "Journal of Microscopy", title = "Microstructural characteristics of calcium hydroxyapatite/poly-L-lactide based composites", pages = "248-243", number = "2", volume = "196", doi = "10.1046/j.1365-2818.1999.00623.x" }
Ignjatović, N., Plavšić, M. B., Miljković, M., Zivković, L.,& Uskoković, D.. (1999). Microstructural characteristics of calcium hydroxyapatite/poly-L-lactide based composites. in Journal of Microscopy Wiley, Hoboken., 196(2), 243-248. https://doi.org/10.1046/j.1365-2818.1999.00623.x
Ignjatović N, Plavšić MB, Miljković M, Zivković L, Uskoković D. Microstructural characteristics of calcium hydroxyapatite/poly-L-lactide based composites. in Journal of Microscopy. 1999;196(2):243-248. doi:10.1046/j.1365-2818.1999.00623.x .
Ignjatović, NL, Plavšić, Milenko B., Miljković, Miroslav, Zivković, LM, Uskoković, Dragan, "Microstructural characteristics of calcium hydroxyapatite/poly-L-lactide based composites" in Journal of Microscopy, 196, no. 2 (1999):243-248, https://doi.org/10.1046/j.1365-2818.1999.00623.x . .