Influence of the structural changes on cavitation resistance of Al18SiCuMg alloy produced by rheocasting process
Uticaj strukturnih promena na kavitacionu otpornost Al18SiCuMg legure proizvedene reokasting procesom
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
The influence of stirring speeds of 1000 and 1500 r/min on the microstructure of Al18SiCuMg alloy was investigated. The smaller size of Si particles of rheocast sample obtained by higher cooling rate and higher stirring speed was achieved. According to the results of cavitation test, the cavitation rate of the rheocast sample produced by 1500 r/min is lower than that of the rheocast sample obtained by 1000 r/min. The different results show that the mass loss as a function of time can be approximated either by liner or quadratic equations.
U radu je ispitivan uticaj brzine mešanja od 1000 i 1500 obrta/min na mikrostrukturu Al18SiCuMg legure. Manja veličina Si čestica u reokast uzorcima postignuta je pri većoj brzini hlađenja i većoj brzini mešanja. Prema rezultatima kavitacionog ispitivanja, kavitaciona brzina reokast uzoraka dobijenih pri brzini mešanja od 1500 obrta/min je niža u odnosu na reokast uzorke dobijene pri brzini mešanja od 1000 obrta/min. Rezultati ispitivanja pokazuju da se gubitak mase u funkciji vremena može aproksimirati ili pomoću linearnih ili kvadratnih jednačina.
Ključne reči:
Al18SiCuMg alloy / rheocasting / microstructure / cavitation rate / Al18SiCuMg legure / reokasting / mikrostruktura / kavitaciona brzinaIzvor:
Zaštita materijala, 2015, 56, 4, 505-509Izdavač:
- Engineering Society for Corrosion, Belgrade, Serbia
Institucija/grupa
Tehnološko-metalurški fakultetTY - JOUR AU - Ćosić, Milena AU - Dojčinović, Marina AU - Boljanović, Slobodanka PY - 2015 UR - http://TechnoRep.tmf.bg.ac.rs/handle/123456789/2949 AB - The influence of stirring speeds of 1000 and 1500 r/min on the microstructure of Al18SiCuMg alloy was investigated. The smaller size of Si particles of rheocast sample obtained by higher cooling rate and higher stirring speed was achieved. According to the results of cavitation test, the cavitation rate of the rheocast sample produced by 1500 r/min is lower than that of the rheocast sample obtained by 1000 r/min. The different results show that the mass loss as a function of time can be approximated either by liner or quadratic equations. AB - U radu je ispitivan uticaj brzine mešanja od 1000 i 1500 obrta/min na mikrostrukturu Al18SiCuMg legure. Manja veličina Si čestica u reokast uzorcima postignuta je pri većoj brzini hlađenja i većoj brzini mešanja. Prema rezultatima kavitacionog ispitivanja, kavitaciona brzina reokast uzoraka dobijenih pri brzini mešanja od 1500 obrta/min je niža u odnosu na reokast uzorke dobijene pri brzini mešanja od 1000 obrta/min. Rezultati ispitivanja pokazuju da se gubitak mase u funkciji vremena može aproksimirati ili pomoću linearnih ili kvadratnih jednačina. PB - Engineering Society for Corrosion, Belgrade, Serbia T2 - Zaštita materijala T1 - Influence of the structural changes on cavitation resistance of Al18SiCuMg alloy produced by rheocasting process T1 - Uticaj strukturnih promena na kavitacionu otpornost Al18SiCuMg legure proizvedene reokasting procesom EP - 509 IS - 4 SP - 505 VL - 56 DO - 10.5937/ZasMat1504505c ER -
@article{ author = "Ćosić, Milena and Dojčinović, Marina and Boljanović, Slobodanka", year = "2015", abstract = "The influence of stirring speeds of 1000 and 1500 r/min on the microstructure of Al18SiCuMg alloy was investigated. The smaller size of Si particles of rheocast sample obtained by higher cooling rate and higher stirring speed was achieved. According to the results of cavitation test, the cavitation rate of the rheocast sample produced by 1500 r/min is lower than that of the rheocast sample obtained by 1000 r/min. The different results show that the mass loss as a function of time can be approximated either by liner or quadratic equations., U radu je ispitivan uticaj brzine mešanja od 1000 i 1500 obrta/min na mikrostrukturu Al18SiCuMg legure. Manja veličina Si čestica u reokast uzorcima postignuta je pri većoj brzini hlađenja i većoj brzini mešanja. Prema rezultatima kavitacionog ispitivanja, kavitaciona brzina reokast uzoraka dobijenih pri brzini mešanja od 1500 obrta/min je niža u odnosu na reokast uzorke dobijene pri brzini mešanja od 1000 obrta/min. Rezultati ispitivanja pokazuju da se gubitak mase u funkciji vremena može aproksimirati ili pomoću linearnih ili kvadratnih jednačina.", publisher = "Engineering Society for Corrosion, Belgrade, Serbia", journal = "Zaštita materijala", title = "Influence of the structural changes on cavitation resistance of Al18SiCuMg alloy produced by rheocasting process, Uticaj strukturnih promena na kavitacionu otpornost Al18SiCuMg legure proizvedene reokasting procesom", pages = "509-505", number = "4", volume = "56", doi = "10.5937/ZasMat1504505c" }
Ćosić, M., Dojčinović, M.,& Boljanović, S.. (2015). Influence of the structural changes on cavitation resistance of Al18SiCuMg alloy produced by rheocasting process. in Zaštita materijala Engineering Society for Corrosion, Belgrade, Serbia., 56(4), 505-509. https://doi.org/10.5937/ZasMat1504505c
Ćosić M, Dojčinović M, Boljanović S. Influence of the structural changes on cavitation resistance of Al18SiCuMg alloy produced by rheocasting process. in Zaštita materijala. 2015;56(4):505-509. doi:10.5937/ZasMat1504505c .
Ćosić, Milena, Dojčinović, Marina, Boljanović, Slobodanka, "Influence of the structural changes on cavitation resistance of Al18SiCuMg alloy produced by rheocasting process" in Zaštita materijala, 56, no. 4 (2015):505-509, https://doi.org/10.5937/ZasMat1504505c . .